IS 6911 X02Cr19Ni10 vs ASTM A959 304LN

Strong Match — 90.7% match based on chemical composition and mechanical property overlap.

IS 6911 X02Cr19Ni10 (IS 6911:1992) and ASTM A959 304LN (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 6911 X02Cr19Ni10 is typically used for stainless and heat-resisting steel plate, sheet and strip (clause 1.1), while ASTM A959 304LN is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 6911 X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 304LN is defined under ASTM International, originating from United States.

As per chemical composition, IS 6911 X02Cr19Ni10 vs ASTM A959 304LN is a 90.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 90.7%.

Frequently Compared With IS 6911 X02Cr19Ni10:
EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4006
Match Breakdown
CHEMISTRY MATCH
90.7%
MECHANICAL MATCH
No shared data
OVERALL
90.7%
Specifications
Property IS 6911 X02Cr19Ni10 ASTM A959 304LN
Standard IS 6911:1992 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.03 <=0.030
Cr (%) 17.5-20.0 18.0-20.0
Mn (%) <=2.0 <=2.00
Ni (%) 8.0-12.0 8.0-11.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.0 <=1.00
N (%) Not specified 0.10-0.16
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6911 X02Cr19Ni10 ASTM A959 304LN
Bend Test (180 deg) Not required Not specified
Elongation (50 mm, annealed) >=40% Not specified
Hardness (annealed, max) 192 HBS, 88 HRB Not specified
Tensile Strength (annealed) >=440 MPa Not specified
Yield Strength (0.2% proof, annealed) >=180 MPa Not specified
Typical Applications
IS 6911 X02Cr19Ni10
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
ASTM A959 304LN
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 6911 X02Cr19Ni10 Be Substituted With ASTM A959 304LN?
IS 6911 X02Cr19Ni10 and ASTM A959 304LN overlap closely enough on chemistry and mechanical properties that ASTM A959 304LN is often considered as a substitute for IS 6911 X02Cr19Ni10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 6911 X02Cr19Ni10
0 active listings and RFQs →
ASTM A959 304LN
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6911 X02Cr19Ni10 and ASTM A959 304LN?
ASTM A959 304LN specifies N which is not specified for IS 6911 X02Cr19Ni10.
Can IS 6911 X02Cr19Ni10 be substituted with ASTM A959 304LN?
IS 6911 X02Cr19Ni10 and ASTM A959 304LN overlap closely enough on chemistry and mechanical properties that ASTM A959 304LN is often considered as a substitute for IS 6911 X02Cr19Ni10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.