Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 6911 X07Cr17Mn12Ni4 (IS 6911:1992) and GOST 5632 12Kh13 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 6911 X07Cr17Mn12Ni4 is typically used for stainless and heat-resisting steel plate, sheet and strip (clause 1.1), while GOST 5632 12Kh13 is commonly used for turbine blades, pump shafts, fasteners, cutlery.
IS 6911 X07Cr17Mn12Ni4 is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, IS 6911 X07Cr17Mn12Ni4 vs GOST 5632 12Kh13 is a 64.4% match.
As per mechanical properties, the match is 50%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6911 X07Cr17Mn12Ni4
GOST 5632 12Kh13
Bend Test (180 deg)
Not required
Not specified
Elongation (50 mm, annealed)
>=40%
Not specified
Hardness (annealed, max)
217 HBS, 95 HRB
Not specified
Tensile Strength (annealed)
>=540 MPa
Not specified
Yield Strength (0.2% proof, annealed)
>=260 MPa
Not specified
Tensile Strength
Not specified
≥540 MPa (annealed)
Hardness HRC
Not specified
36–45 (hardened)
Typical Applications
IS 6911 X07Cr17Mn12Ni4
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
GOST 5632 12Kh13
Turbine blades, pump shafts, fasteners, cutlery
Key Differences
IS 6911 X07Cr17Mn12Ni4 specifies P, S which are not specified for GOST 5632 12Kh13.
Can IS 6911 X07Cr17Mn12Ni4 Be Substituted With GOST 5632 12Kh13?
IS 6911 X07Cr17Mn12Ni4 and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 6911 X07Cr17Mn12Ni4 and GOST 5632 12Kh13?
IS 6911 X07Cr17Mn12Ni4 specifies P, S which are not specified for GOST 5632 12Kh13.
Can IS 6911 X07Cr17Mn12Ni4 be substituted with GOST 5632 12Kh13?
IS 6911 X07Cr17Mn12Ni4 and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.