IS 6911 X10Cr17Mn6Ni4N20 vs EN 10088-1 1.4006

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 6911 X10Cr17Mn6Ni4N20 (IS 6911:1992) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 6911 X10Cr17Mn6Ni4N20 is typically used for stainless and heat-resisting steel plate, sheet and strip (clause 1.1), while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. IS 6911 X10Cr17Mn6Ni4N20 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6911 X10Cr17Mn6Ni4N20 vs EN 10088-1 1.4006 is a 60.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 6911 X10Cr17Mn6Ni4N20:
ASTM A959 201 ASTM A959 202 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH ASTM A959 205 GOST 5632 08X18H10 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
60.1%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 6911 X10Cr17Mn6Ni4N20 EN 10088-1 1.4006
Standard IS 6911:1992 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.20 0.08–0.15
Cr (%) 16.0-18.0 11.5–13.5
Mn (%) 4.0-8.0 ≤1.50
N (%) 0.05-0.20 Not specified
Ni (%) 3.5-5.5 ≤0.75
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Si (%) <=1.0 ≤1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6911 X10Cr17Mn6Ni4N20 EN 10088-1 1.4006
Bend Test (180 deg) Not required Not specified
Elongation (50 mm, annealed) >=40% Not specified
Hardness (annealed, max) 217 HBS, 95 HRB Not specified
Tensile Strength (annealed) >=640 MPa Not specified
Yield Strength (0.2% proof, annealed) >=300 MPa Not specified
Tensile Strength Not specified ≥540 MPa (annealed)
Hardness HRC Not specified 36–45 (hardened)
Elongation Not specified ≥18%
Typical Applications
IS 6911 X10Cr17Mn6Ni4N20
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can IS 6911 X10Cr17Mn6Ni4N20 Be Substituted With EN 10088-1 1.4006?
IS 6911 X10Cr17Mn6Ni4N20 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 6911 X10Cr17Mn6Ni4N20
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
IS 6911 X10Cr17Mn6Ni4N20
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6911 X10Cr17Mn6Ni4N20 and EN 10088-1 1.4006?
IS 6911 X10Cr17Mn6Ni4N20 specifies N, P, S which are not specified for EN 10088-1 1.4006.
Can IS 6911 X10Cr17Mn6Ni4N20 be substituted with EN 10088-1 1.4006?
IS 6911 X10Cr17Mn6Ni4N20 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.