Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 6911 X10Cr17Mn6Ni4N20 (IS 6911:1992) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 6911 X10Cr17Mn6Ni4N20 is typically used for stainless and heat-resisting steel plate, sheet and strip (clause 1.1), while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications.
IS 6911 X10Cr17Mn6Ni4N20 is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, IS 6911 X10Cr17Mn6Ni4N20 vs GOST 5632 08X18H10 is a 62.1% match.
As per mechanical properties, the match is 33.3%.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With IS 6911 X10Cr17Mn6Ni4N20:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6911 X10Cr17Mn6Ni4N20
GOST 5632 08X18H10
Bend Test (180 deg)
Not required
Not specified
Elongation (50 mm, annealed)
>=40%
Not specified
Hardness (annealed, max)
217 HBS, 95 HRB
Not specified
Tensile Strength (annealed)
>=640 MPa
Not specified
Yield Strength (0.2% proof, annealed)
>=300 MPa
Not specified
Tensile Strength
Not specified
≥520 MPa
Yield Strength
Not specified
≥205 MPa
Elongation
Not specified
≥40%
Typical Applications
IS 6911 X10Cr17Mn6Ni4N20
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
IS 6911 X10Cr17Mn6Ni4N20 specifies N which is not specified for GOST 5632 08X18H10.
Can IS 6911 X10Cr17Mn6Ni4N20 Be Substituted With GOST 5632 08X18H10?
IS 6911 X10Cr17Mn6Ni4N20 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 6911 X10Cr17Mn6Ni4N20 and GOST 5632 08X18H10?
IS 6911 X10Cr17Mn6Ni4N20 specifies N which is not specified for GOST 5632 08X18H10.
Can IS 6911 X10Cr17Mn6Ni4N20 be substituted with GOST 5632 08X18H10?
IS 6911 X10Cr17Mn6Ni4N20 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.