JIS G4051 S35C vs BS 970 (Part 1) 080A20

Close Alternative — 81.8% match based on chemical composition and mechanical property overlap.

JIS G4051 S35C (JIS G4051:2009) and BS 970 (Part 1) 080A20 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Carbon Steel category. JIS G4051 S35C is typically used for crankshafts, axles, gears, bolts, while BS 970 (Part 1) 080A20 is commonly used for used for nuts, bolts, hydraulic fittings, precision turned parts, sleeves, and couplings.. JIS G4051 S35C is defined under Japanese Industrial Standards (JIS), originating from Japan, while BS 970 (Part 1) 080A20 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, JIS G4051 S35C vs BS 970 (Part 1) 080A20 is a 81.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 81.8%.

Frequently Compared With JIS G4051 S35C:
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 055M15 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 060A32 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10
Match Breakdown
CHEMISTRY MATCH
81.8%
MECHANICAL MATCH
No shared data
OVERALL
81.8%
Specifications
Property JIS G4051 S35C BS 970 (Part 1) 080A20
Standard JIS G4051:2009 BS 970 (Part 1):1991
Category Carbon Steel Carbon Steel
C (%) 0.32-0.38 0.18-0.23
Si (%) 0.15-0.35 Not specified
Mn (%) 0.60-0.90 0.70-0.90
S (%) <=0.035 Not specified
P (%) <=0.030 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4051 S35C BS 970 (Part 1) 080A20
Tensile Strength >=530 MPa Not specified
Elongation >=19% Not specified
Hardness <=167 HB Not specified
Typical Applications
JIS G4051 S35C
Crankshafts, axles, gears, bolts
BS 970 (Part 1) 080A20
Used for nuts, bolts, hydraulic fittings, precision turned parts, sleeves, and couplings.
Key Differences
Can JIS G4051 S35C Be Substituted With BS 970 (Part 1) 080A20?
JIS G4051 S35C and BS 970 (Part 1) 080A20 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
JIS G4051 S35C
Round Bar → (3 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5600–6300 mm (220.47–248.03 in)
BS 970 (Part 1) 080A20
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 4800–6600 mm (188.98–259.84 in)
On M-EX Right Now
JIS G4051 S35C
3 active listings and RFQs →
BS 970 (Part 1) 080A20
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4051 S35C and BS 970 (Part 1) 080A20?
JIS G4051 S35C specifies Si, S, P which are not specified for BS 970 (Part 1) 080A20.
Can JIS G4051 S35C be substituted with BS 970 (Part 1) 080A20?
JIS G4051 S35C and BS 970 (Part 1) 080A20 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.