JIS G4102 SNC815 vs IS 1570 (Part 7) 10Cr36Mo10H

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

JIS G4102 SNC815 (JIS G 4102:1979) and IS 1570 (Part 7) 10Cr36Mo10H (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Alloy Steel category. JIS G4102 SNC815 is typically used for heavily stressed gears, differential components, while IS 1570 (Part 7) 10Cr36Mo10H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. JIS G4102 SNC815 is defined under Japanese Industrial Standards (JIS), originating from Japan, while IS 1570 (Part 7) 10Cr36Mo10H is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, JIS G4102 SNC815 vs IS 1570 (Part 7) 10Cr36Mo10H is a 60.4% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With JIS G4102 SNC815:
NF A35-565 100C6 UNI 11234 100Cr6 GOST 4543 12HN3A GB/T 3077 12Cr2Ni4A IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 07Cr4Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6
Other Alloy Steel Grades to Compare With JIS G4102 SNC815:
EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
60.4%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property JIS G4102 SNC815 IS 1570 (Part 7) 10Cr36Mo10H
Standard JIS G 4102:1979 IS 1570 (Part 7):1992
Category Alloy Steel Alloy Steel
C (%) 0.12–0.18 <=0.15
Si (%) 0.15–0.35 0.25-1.0
Mn (%) 0.30–0.60 0.30-0.60
Cr (%) 0.60–1.00 8.00-10.00
Ni (%) 3.00–3.50 Not specified
P (%) ≤0.030 <=0.040
S (%) ≤0.030 <=0.030
Mo (%) Not specified 0.90-1.10
Al (metallic) (%) Not specified <=0.02
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4102 SNC815 IS 1570 (Part 7) 10Cr36Mo10H
Tensile Strength ≥980 MPa 410-560 MPa
Case Hardness HRC 60–65 Not specified
Yield Strength Not specified >=135 MPa (0.2 % proof stress)
Elongation Not specified >=20%
Condition Not specified Pipes, A, thickness - (first row of Table 3)
Typical Applications
JIS G4102 SNC815
Heavily stressed gears, differential components
IS 1570 (Part 7) 10Cr36Mo10H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can JIS G4102 SNC815 Be Substituted With IS 1570 (Part 7) 10Cr36Mo10H?
JIS G4102 SNC815 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
JIS G4102 SNC815
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 4900–5900 mm (192.91–232.28 in)
IS 1570 (Part 7) 10Cr36Mo10H
No active listings currently.
On M-EX Right Now
JIS G4102 SNC815
2 active listings and RFQs →
IS 1570 (Part 7) 10Cr36Mo10H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4102 SNC815 and IS 1570 (Part 7) 10Cr36Mo10H?
JIS G4102 SNC815 specifies Ni which is not specified for IS 1570 (Part 7) 10Cr36Mo10H. IS 1570 (Part 7) 10Cr36Mo10H specifies Mo, Al (metallic) which are not specified for JIS G4102 SNC815.
Can JIS G4102 SNC815 be substituted with IS 1570 (Part 7) 10Cr36Mo10H?
JIS G4102 SNC815 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.