Strong Match — 97.2% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS316Ti (JIS G4304:2021) and ASTM A959 316Cb (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS316Ti is typically used for hot-rolled stainless steel plates and strips, while ASTM A959 316Cb is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). JIS G4304 SUS316Ti is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 316Cb is defined under ASTM International, originating from United States.

As per chemical composition, JIS G4304 SUS316Ti vs ASTM A959 316Cb is a 97.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 97.2%.

Frequently Compared With JIS G4304 SUS316Ti:
IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10
Match Breakdown
CHEMISTRY MATCH
97.2%
MECHANICAL MATCH
No shared data
OVERALL
97.2%
Specifications
Property JIS G4304 SUS316Ti ASTM A959 316Cb
Standard JIS G4304:2021 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Ni (%) 10.00-14.00 10.0-14.0
Cr (%) 16.00-18.00 16.0-18.0
Mo (%) 2.00-3.00 2.00-3.00
N (%) Not specified <=0.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS316Ti ASTM A959 316Cb
Tensile Strength >=520 MPa Not specified
Yield Strength >=205 MPa Not specified
Elongation >=40% Not specified
Hardness <=187 HB Not specified
Condition Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4304 SUS316Ti
Hot-rolled stainless steel plates and strips
ASTM A959 316Cb
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can JIS G4304 SUS316Ti Be Substituted With ASTM A959 316Cb?
JIS G4304 SUS316Ti and ASTM A959 316Cb overlap closely enough on chemistry and mechanical properties that ASTM A959 316Cb is often considered as a substitute for JIS G4304 SUS316Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
JIS G4304 SUS316Ti
0 active listings and RFQs →
ASTM A959 316Cb
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS316Ti and ASTM A959 316Cb?
ASTM A959 316Cb specifies N which is not specified for JIS G4304 SUS316Ti.
Can JIS G4304 SUS316Ti be substituted with ASTM A959 316Cb?
JIS G4304 SUS316Ti and ASTM A959 316Cb overlap closely enough on chemistry and mechanical properties that ASTM A959 316Cb is often considered as a substitute for JIS G4304 SUS316Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.