Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
JIS G4304 SUS316Ti (JIS G4304:2021) and IS 1570 (Part 7) 12Cr13H (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4304 SUS316Ti is typically used for hot-rolled stainless steel plates and strips, while IS 1570 (Part 7) 12Cr13H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature.
JIS G4304 SUS316Ti is defined under Japanese Industrial Standards (JIS), originating from Japan, while IS 1570 (Part 7) 12Cr13H is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, JIS G4304 SUS316Ti vs IS 1570 (Part 7) 12Cr13H is a 63.6% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4304 SUS316Ti
IS 1570 (Part 7) 12Cr13H
Tensile Strength
>=520 MPa
470-670 MPa
Yield Strength
>=205 MPa
>=265 MPa (0.2 % proof stress)
Elongation
>=40%
>=20%
Hardness
<=187 HB
Not specified
Condition
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Bars, forgings, plates, A, thickness up to 160 (first row of Table 3)
Typical Applications
JIS G4304 SUS316Ti
Hot-rolled stainless steel plates and strips
IS 1570 (Part 7) 12Cr13H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
JIS G4304 SUS316Ti specifies Mo which is not specified for IS 1570 (Part 7) 12Cr13H.
Can JIS G4304 SUS316Ti Be Substituted With IS 1570 (Part 7) 12Cr13H?
JIS G4304 SUS316Ti and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between JIS G4304 SUS316Ti and IS 1570 (Part 7) 12Cr13H?
JIS G4304 SUS316Ti specifies Mo which is not specified for IS 1570 (Part 7) 12Cr13H.
Can JIS G4304 SUS316Ti be substituted with IS 1570 (Part 7) 12Cr13H?
JIS G4304 SUS316Ti and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.