JIS G4304 SUS316Ti vs IS 1570 (Part 7) 11Cr17Ni13W3TiH

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS316Ti (JIS G4304:2021) and IS 1570 (Part 7) 11Cr17Ni13W3TiH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS316Ti is typically used for hot-rolled stainless steel plates and strips, while IS 1570 (Part 7) 11Cr17Ni13W3TiH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. JIS G4304 SUS316Ti is defined under Japanese Industrial Standards (JIS), originating from Japan, while IS 1570 (Part 7) 11Cr17Ni13W3TiH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, JIS G4304 SUS316Ti vs IS 1570 (Part 7) 11Cr17Ni13W3TiH is a 62.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With JIS G4304 SUS316Ti:
IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H ASTM A959 .- EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10
Match Breakdown
CHEMISTRY MATCH
62.1%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property JIS G4304 SUS316Ti IS 1570 (Part 7) 11Cr17Ni13W3TiH
Standard JIS G4304:2021 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) <=0.08 0.07-0.15
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=1.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Ni (%) 10.00-14.00 12.00-14.50
Cr (%) 16.00-18.00 15.5-17.50
Mo (%) 2.00-3.00 Not specified
W (%) Not specified 2.5-3.5
Ti (%) Not specified >=4xC, <=0.80
B (%) Not specified <=0.0006
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS316Ti IS 1570 (Part 7) 11Cr17Ni13W3TiH
Tensile Strength >=520 MPa 600-800 MPa
Yield Strength >=205 MPa >=390 MPa (0.2 % proof stress)
Elongation >=40% >=25%
Hardness <=187 HB Not specified
Condition Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser Bars, forgings, pipes, hot cold worked, thickness up to 60 (first row of Table 3)
Typical Applications
JIS G4304 SUS316Ti
Hot-rolled stainless steel plates and strips
IS 1570 (Part 7) 11Cr17Ni13W3TiH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can JIS G4304 SUS316Ti Be Substituted With IS 1570 (Part 7) 11Cr17Ni13W3TiH?
JIS G4304 SUS316Ti and IS 1570 (Part 7) 11Cr17Ni13W3TiH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
JIS G4304 SUS316Ti
0 active listings and RFQs →
IS 1570 (Part 7) 11Cr17Ni13W3TiH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS316Ti and IS 1570 (Part 7) 11Cr17Ni13W3TiH?
JIS G4304 SUS316Ti specifies Mo which is not specified for IS 1570 (Part 7) 11Cr17Ni13W3TiH. IS 1570 (Part 7) 11Cr17Ni13W3TiH specifies W, Ti, B which are not specified for JIS G4304 SUS316Ti.
Can JIS G4304 SUS316Ti be substituted with IS 1570 (Part 7) 11Cr17Ni13W3TiH?
JIS G4304 SUS316Ti and IS 1570 (Part 7) 11Cr17Ni13W3TiH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.