Strong Match — 96.8% match
based on chemical composition and mechanical property overlap.
JIS G4304 SUS403 (JIS G4304:2021) and JIS G4304 SUS410 (JIS G4304:2021) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4304 SUS403 is typically used for hot-rolled stainless steel plates and strips, while JIS G4304 SUS410 is commonly used for hot-rolled stainless steel plates and strips.
JIS G4304 SUS403 is defined under Japanese Industrial Standards (JIS), originating from Japan, while JIS G4304 SUS410 is defined under Japanese Industrial Standards (JIS), originating from Japan.
As per chemical composition, JIS G4304 SUS403 vs JIS G4304 SUS410 is a 95.1% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 96.8%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4304 SUS403
JIS G4304 SUS410
Tensile Strength
>=440 MPa
>=440 MPa
Yield Strength
>=205 MPa
>=205 MPa
Elongation
>=20%
>=20%
Hardness
<=201 HB
<=201 HB
Condition
Annealed plate and strip; proof strength applies only when specified by the purchaser
Annealed plate and strip; proof strength applies only when specified by the purchaser
Typical Applications
JIS G4304 SUS403
Hot-rolled stainless steel plates and strips
JIS G4304 SUS410
Hot-rolled stainless steel plates and strips
Can JIS G4304 SUS403 Be Substituted With JIS G4304 SUS410?
JIS G4304 SUS403 and JIS G4304 SUS410 overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS410 is often considered as a substitute for JIS G4304 SUS403 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between JIS G4304 SUS403 and JIS G4304 SUS410?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4304 SUS403 be substituted with JIS G4304 SUS410?
JIS G4304 SUS403 and JIS G4304 SUS410 overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS410 is often considered as a substitute for JIS G4304 SUS403 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.