JIS G4304 SUS410L vs ASTM A959 S40977

Close Alternative — 84.5% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS410L (JIS G4304:2021) and ASTM A959 S40977 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS410L is typically used for hot-rolled stainless steel plates and strips, while ASTM A959 S40977 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). JIS G4304 SUS410L is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 S40977 is defined under ASTM International, originating from United States.

As per chemical composition, JIS G4304 SUS410L vs ASTM A959 S40977 is a 84.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 84.5%.

Frequently Compared With JIS G4304 SUS410L:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
84.5%
MECHANICAL MATCH
No shared data
OVERALL
84.5%
Specifications
Property JIS G4304 SUS410L ASTM A959 S40977
Standard JIS G4304:2021 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=1.50
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.015
Cr (%) 11.00-13.50 10.5-12.5
Ni (%) <=0.60 0.30-1.00
N (%) Not specified <=0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS410L ASTM A959 S40977
Tensile Strength >=360 MPa Not specified
Yield Strength >=195 MPa Not specified
Elongation >=22% Not specified
Hardness <=183 HB Not specified
Condition Annealed plate and strip; proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4304 SUS410L
Hot-rolled stainless steel plates and strips
ASTM A959 S40977
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can JIS G4304 SUS410L Be Substituted With ASTM A959 S40977?
JIS G4304 SUS410L and ASTM A959 S40977 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
JIS G4304 SUS410L
0 active listings and RFQs →
ASTM A959 S40977
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS410L and ASTM A959 S40977?
ASTM A959 S40977 specifies N which is not specified for JIS G4304 SUS410L.
Can JIS G4304 SUS410L be substituted with ASTM A959 S40977?
JIS G4304 SUS410L and ASTM A959 S40977 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.