JIS G4304 SUS410L vs EN 10088-1 X2CrNi12

Close Alternative — 84.5% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS410L (JIS G4304:2021) and EN 10088-1 X2CrNi12 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS410L is defined under Japanese Industrial Standards (JIS), originating from Japan, while EN 10088-1 X2CrNi12 is defined under European Standard (EN), originating from Europe.

As per chemical composition, JIS G4304 SUS410L vs EN 10088-1 X2CrNi12 is a 84.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 84.5%.

Frequently Compared With JIS G4304 SUS410L:
ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
84.5%
MECHANICAL MATCH
No shared data
OVERALL
84.5%
Specifications
Property JIS G4304 SUS410L EN 10088-1 X2CrNi12
Standard JIS G4304:2021 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=1.50
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.015
Cr (%) 11.00-13.50 10.5-12.5
Ni (%) <=0.60 0.30-1.00
N (%) Not specified <=0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS410L EN 10088-1 X2CrNi12
Tensile Strength >=360 MPa Not specified
Yield Strength >=195 MPa Not specified
Elongation >=22% Not specified
Hardness <=183 HB Not specified
Condition Annealed plate and strip; proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4304 SUS410L
Hot-rolled stainless steel plates and strips
EN 10088-1 X2CrNi12
Not documented
Key Differences
Can JIS G4304 SUS410L Be Substituted With EN 10088-1 X2CrNi12?
JIS G4304 SUS410L and EN 10088-1 X2CrNi12 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
JIS G4304 SUS410L
0 active listings and RFQs →
EN 10088-1 X2CrNi12
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS410L and EN 10088-1 X2CrNi12?
EN 10088-1 X2CrNi12 specifies N which is not specified for JIS G4304 SUS410L.
Can JIS G4304 SUS410L be substituted with EN 10088-1 X2CrNi12?
JIS G4304 SUS410L and EN 10088-1 X2CrNi12 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.