JIS G4304 SUS630 vs ASTM A959 431

Close Alternative — 76.3% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS630 (JIS G4304:2021) and ASTM A959 431 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS630 is typically used for hot-rolled stainless steel plates and strips, while ASTM A959 431 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). JIS G4304 SUS630 is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 431 is defined under ASTM International, originating from United States.

As per chemical composition, JIS G4304 SUS630 vs ASTM A959 431 is a 76.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 76.3%.

Frequently Compared With JIS G4304 SUS630:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
76.3%
MECHANICAL MATCH
No shared data
OVERALL
76.3%
Specifications
Property JIS G4304 SUS630 ASTM A959 431
Standard JIS G4304:2021 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.07 <=0.20
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Ni (%) 3.00-5.00 1.25-2.50
Cr (%) 15.00-17.50 15.0-17.0
Cu (%) 3.00-5.00 Not specified
Nb (%) 0.15-0.45 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS630 ASTM A959 431
Hardness <=363 HB Not specified
Condition Solution heat treated plate and strip (no strength values specified; aged conditions are in the blocks) Not specified
Typical Applications
JIS G4304 SUS630
Hot-rolled stainless steel plates and strips
ASTM A959 431
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can JIS G4304 SUS630 Be Substituted With ASTM A959 431?
JIS G4304 SUS630 and ASTM A959 431 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
JIS G4304 SUS630
0 active listings and RFQs →
ASTM A959 431
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS630 and ASTM A959 431?
JIS G4304 SUS630 specifies Cu, Nb which are not specified for ASTM A959 431.
Can JIS G4304 SUS630 be substituted with ASTM A959 431?
JIS G4304 SUS630 and ASTM A959 431 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.