Strong Match — 92.5% match
based on chemical composition and mechanical property overlap.
JIS G4304 SUSXM7 (JIS G4304:2021) and ASTM A959 347 (ASTM A959:2011) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4304 SUSXM7 is typically used for hot-rolled stainless steel plates and strips, while ASTM A959 347 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1).
JIS G4304 SUSXM7 is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 347 is defined under ASTM International, originating from United States.
As per chemical composition, JIS G4304 SUSXM7 vs ASTM A959 347 is a 92.5% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 92.5%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4304 SUSXM7
ASTM A959 347
Tensile Strength
>=450 MPa
Not specified
Yield Strength
>=155 MPa
Not specified
Elongation
>=40%
Not specified
Hardness
<=187 HB
Not specified
Condition
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Not specified
Typical Applications
JIS G4304 SUSXM7
Hot-rolled stainless steel plates and strips
ASTM A959 347
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
JIS G4304 SUSXM7 specifies Cu which is not specified for ASTM A959 347.
Can JIS G4304 SUSXM7 Be Substituted With ASTM A959 347?
JIS G4304 SUSXM7 and ASTM A959 347 overlap closely enough on chemistry and mechanical properties that ASTM A959 347 is often considered as a substitute for JIS G4304 SUSXM7 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between JIS G4304 SUSXM7 and ASTM A959 347?
JIS G4304 SUSXM7 specifies Cu which is not specified for ASTM A959 347.
Can JIS G4304 SUSXM7 be substituted with ASTM A959 347?
JIS G4304 SUSXM7 and ASTM A959 347 overlap closely enough on chemistry and mechanical properties that ASTM A959 347 is often considered as a substitute for JIS G4304 SUSXM7 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.