Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
JIS G4305 SUS434 (JIS G4305:2012) and ASTM A959 316H (ASTM A959:2011) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4305 SUS434 is typically used for cold-rolled stainless steel plates, sheet and strip, while ASTM A959 316H is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1).
JIS G4305 SUS434 is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 316H is defined under ASTM International, originating from United States.
As per chemical composition, JIS G4305 SUS434 vs ASTM A959 316H is a 76.1% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 69.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4305 SUS434
ASTM A959 316H
Tensile Strength
>=450 MPa
Not specified
Yield Strength
>=205 MPa
Not specified
Elongation
>=22%
Not specified
Hardness
<=183 HB
Not specified
Condition
Annealed plate and strip; proof strength applies only when specified by the purchaser
Not specified
Typical Applications
JIS G4305 SUS434
Cold-rolled stainless steel plates, sheet and strip
ASTM A959 316H
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can JIS G4305 SUS434 Be Substituted With ASTM A959 316H?
JIS G4305 SUS434 and ASTM A959 316H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between JIS G4305 SUS434 and ASTM A959 316H?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4305 SUS434 be substituted with ASTM A959 316H?
JIS G4305 SUS434 and ASTM A959 316H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.