JIS G4305 SUS630 vs EN 10088-1 X5CrNi17-7

Close Alternative — 73.3% match based on chemical composition and mechanical property overlap.

JIS G4305 SUS630 (JIS G4305:2012) and EN 10088-1 X5CrNi17-7 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. JIS G4305 SUS630 is defined under Japanese Industrial Standards (JIS), originating from Japan, while EN 10088-1 X5CrNi17-7 is defined under European Standard (EN), originating from Europe.

As per chemical composition, JIS G4305 SUS630 vs EN 10088-1 X5CrNi17-7 is a 73.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 73.3%.

Frequently Compared With JIS G4305 SUS630:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH
Other Stainless Steel Grades to Compare With JIS G4305 SUS630:
IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
73.3%
MECHANICAL MATCH
No shared data
OVERALL
73.3%
Specifications
Property JIS G4305 SUS630 EN 10088-1 X5CrNi17-7
Standard JIS G4305:2012 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.07 <=0.07
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=2.00
P (%) <=0.040 <=0.045
S (%) <=0.030 <=0.030
Ni (%) 3.00-5.00 6.0-8.0
Cr (%) 15.00-17.50 16.0-18.0
Cu (%) 3.00-5.00 Not specified
Nb (%) 0.15-0.45 Not specified
N (%) Not specified <=0.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4305 SUS630 EN 10088-1 X5CrNi17-7
Hardness <=363 HB Not specified
Condition Solution heat treated plate and strip (no strength values specified; aged conditions are in the blocks) Not specified
Typical Applications
JIS G4305 SUS630
Cold-rolled stainless steel plates, sheet and strip
EN 10088-1 X5CrNi17-7
Not documented
Key Differences
Can JIS G4305 SUS630 Be Substituted With EN 10088-1 X5CrNi17-7?
JIS G4305 SUS630 and EN 10088-1 X5CrNi17-7 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
JIS G4305 SUS630
0 active listings and RFQs →
EN 10088-1 X5CrNi17-7
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4305 SUS630 and EN 10088-1 X5CrNi17-7?
JIS G4305 SUS630 specifies Cu, Nb which are not specified for EN 10088-1 X5CrNi17-7. EN 10088-1 X5CrNi17-7 specifies N which is not specified for JIS G4305 SUS630.
Can JIS G4305 SUS630 be substituted with EN 10088-1 X5CrNi17-7?
JIS G4305 SUS630 and EN 10088-1 X5CrNi17-7 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.