Strong Match — 85.2% match
based on chemical composition and mechanical property overlap.
JIS G4305 SUS890L (JIS G4305:2012) and ASTM A959 N08700 (ASTM A959:2011) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4305 SUS890L is typically used for cold-rolled stainless steel plates, sheet and strip, while ASTM A959 N08700 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1).
JIS G4305 SUS890L is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 N08700 is defined under ASTM International, originating from United States.
As per chemical composition, JIS G4305 SUS890L vs ASTM A959 N08700 is a 85.2% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 85.2%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4305 SUS890L
ASTM A959 N08700
Tensile Strength
>=490 MPa
Not specified
Yield Strength
>=215 MPa
Not specified
Elongation
>=35%
Not specified
Hardness
<=187 HB
Not specified
Condition
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Not specified
Typical Applications
JIS G4305 SUS890L
Cold-rolled stainless steel plates, sheet and strip
ASTM A959 N08700
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can JIS G4305 SUS890L Be Substituted With ASTM A959 N08700?
JIS G4305 SUS890L and ASTM A959 N08700 overlap closely enough on chemistry and mechanical properties that ASTM A959 N08700 is often considered as a substitute for JIS G4305 SUS890L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between JIS G4305 SUS890L and ASTM A959 N08700?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4305 SUS890L be substituted with ASTM A959 N08700?
JIS G4305 SUS890L and ASTM A959 N08700 overlap closely enough on chemistry and mechanical properties that ASTM A959 N08700 is often considered as a substitute for JIS G4305 SUS890L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.