Post Stock Login Register

JIS G4801 SUP9 vs EN 10083-3 51CrV4

Minimal Match — 47.4% match based on chemical composition and mechanical property overlap.

JIS G4801 SUP9 (JIS G 4801:2005) and EN 10083-3 51CrV4 (EN 10083-3:2006) are both steel grades. Both fall under the Spring Steel category. JIS G4801 SUP9 is typically used for automotive leaf springs, suspension springs, while EN 10083-3 51CrV4 is commonly used for valve springs, clutch springs, high duty coil springs. JIS G4801 SUP9 is defined under Japanese Industrial Standards (JIS), originating from Japan, while EN 10083-3 51CrV4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, JIS G4801 SUP9 vs EN 10083-3 51CrV4 is a 71% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 47.4%.

Frequently Compared With JIS G4801 SUP9:
EN 10089 55Cr3 EN 10089 50CrV4 EN 10089 55Si7 GB/T 1222 55CrMnA IS 3431 50Cr4V2 IS 3195 113C6 IS 3195 50Cr4V2 EN 10083-1 51CrV4 IS 3195 52Cr4Mo2V EN 10083-1 51CrV4 IS 5517 55Cr3 IS 1570 (Part 4) 55Si7
Match Breakdown
CHEMISTRY MATCH
71%
MECHANICAL MATCH
0%
OVERALL
47.4%
Specifications
Property JIS G4801 SUP9 EN 10083-3 51CrV4
Standard JIS G 4801:2005 EN 10083-3:2006
Category Spring Steel Spring Steel
C (%) 0.52–0.60 0.47-0.55
Mn (%) 0.65–0.95 0.70-1.10
Cr (%) 0.65–0.95 0.90-1.20
Si (%) 0.15–0.35 <=0.40
P (%) ≤0.030 <=0.025
S (%) ≤0.030 <=0.025
V (%) Not specified 0.10-0.25
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4801 SUP9 EN 10083-3 51CrV4
Tensile Strength 1180 MPa min (oil hardened) 1100 to 1300 MPa
Yield Strength ≥1030 MPa 900 MPa min
Elongation ≥7% 9% min
Hardness 363–429 HB Soft annealed (+A): 248 HBW max
Condition Not specified Quenched and tempered (+QT), ruling section d <= 16 mm
Typical Applications
JIS G4801 SUP9
Automotive leaf springs, suspension springs
EN 10083-3 51CrV4
Valve springs, clutch springs, high duty coil springs
Key Differences
Can JIS G4801 SUP9 Be Substituted With EN 10083-3 51CrV4?
JIS G4801 SUP9 and EN 10083-3 51CrV4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
JIS G4801 SUP9
Round Bar → (4 listings)
Diameter: 30–35 mm (1.18–1.38 in)
Length: 3900–6700 mm (153.54–263.78 in)
EN 10083-3 51CrV4
Round Bar → (3 listings)
Diameter: 30–30 mm (1.18–1.18 in)
Length: 6300–7000 mm (248.03–275.59 in)
On M-EX Right Now
JIS G4801 SUP9
4 active listings and RFQs →
EN 10083-3 51CrV4
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4801 SUP9 and EN 10083-3 51CrV4?
EN 10083-3 51CrV4 specifies V which is not specified for JIS G4801 SUP9.
Can JIS G4801 SUP9 be substituted with EN 10083-3 51CrV4?
JIS G4801 SUP9 and EN 10083-3 51CrV4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.