KS D3503 SS400 vs AS/NZS 3679.1 300

Related Material — 65.2% match based on chemical composition and mechanical property overlap.

KS D3503 SS400 (KS D 3503:2016) and AS/NZS 3679.1 300 (AS/NZS 3679.1:2016) are both steel grades. Both fall under the Structural Steel category. KS D3503 SS400 is typically used for structural fabrication,bridges,buildings,machinery frames,general construction,welded structures,plates,sections, while AS/NZS 3679.1 300 is commonly used for hot-rolled structural bars and sections for general structural framing. KS D3503 SS400 is defined under Korean Industrial Standards (KS), originating from South Korea, while AS/NZS 3679.1 300 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, KS D3503 SS400 vs AS/NZS 3679.1 300 is a 92% match. As per mechanical properties, the match is 11.7%. Combined, this makes them a related material overall at 65.2%.

Frequently Compared With KS D3503 SS400:
CSA G40.21 350W AS/NZS 3679.1 350 CSA G40.21 400W GOST 19281 09G2S CSA G40.21 400A CSA G40.21 480W CSA G40.21 260W CSA G40.21 300W ASTM A1008 SS Grade 50 ASTM A1008 SS Grade 80 ASTM A283C ASTM A572 Gr.65
Match Breakdown
CHEMISTRY MATCH
92%
MECHANICAL MATCH
11.7%
OVERALL
65.2%
Specifications
Property KS D3503 SS400 AS/NZS 3679.1 300
Standard KS D 3503:2016 AS/NZS 3679.1:2016
Category Structural Steel Structural Steel
C (%) <=0.25 <=0.22
Mn (%) <=1.50 <=1.70
P (%) <=0.050 <=0.040
S (%) <=0.050 <=0.040
Si (%) Not specified <=0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property KS D3503 SS400 AS/NZS 3679.1 300
Tensile Strength 400-510 MPa 440-600 MPa
Yield Strength 245 MPa min 300 MPa min
Elongation 21-23 % 22% min
Typical Applications
KS D3503 SS400
structural fabrication,bridges,buildings,machinery frames,general construction,welded structures,plates,sections
AS/NZS 3679.1 300
Hot-rolled structural bars and sections for general structural framing
Key Differences
Can KS D3503 SS400 Be Substituted With AS/NZS 3679.1 300?
KS D3503 SS400 and AS/NZS 3679.1 300 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
KS D3503 SS400
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 3000–3700 mm (118.11–145.67 in)
AS/NZS 3679.1 300
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2700–2700 mm (106.3–106.3 in)
On M-EX Right Now
KS D3503 SS400
2 active listings and RFQs →
AS/NZS 3679.1 300
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between KS D3503 SS400 and AS/NZS 3679.1 300?
AS/NZS 3679.1 300 specifies Si which is not specified for KS D3503 SS400.
Can KS D3503 SS400 be substituted with AS/NZS 3679.1 300?
KS D3503 SS400 and AS/NZS 3679.1 300 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.