Related Material — 62.9% match
based on chemical composition and mechanical property overlap.
KS D3867 SCM415 (KS D 3867:2025) and IS 1570 (Part 7) 10Mo6H (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Alloy Steel category.
KS D3867 SCM415 is typically used for gears, shafts, camshafts, piston pins, precision machine components requiring hard surface and tough core., while IS 1570 (Part 7) 10Mo6H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature.
KS D3867 SCM415 is defined under Korean Industrial Standards (KS), originating from South Korea, while IS 1570 (Part 7) 10Mo6H is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, KS D3867 SCM415 vs IS 1570 (Part 7) 10Mo6H is a 62.9% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 62.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
KS D3867 SCM415
IS 1570 (Part 7) 10Mo6H
Tensile Strength
Not specified
>=415 MPa
Yield Strength
Not specified
>=205 MPa (0.2 % proof stress)
Elongation
Not specified
>=30%
Condition
Not specified
Tubes, N+T, thickness - (first row of Table 3)
Typical Applications
KS D3867 SCM415
Gears, shafts, camshafts, piston pins, precision machine components requiring hard surface and tough core.
IS 1570 (Part 7) 10Mo6H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Can KS D3867 SCM415 Be Substituted With IS 1570 (Part 7) 10Mo6H?
KS D3867 SCM415 and IS 1570 (Part 7) 10Mo6H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between KS D3867 SCM415 and IS 1570 (Part 7) 10Mo6H?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can KS D3867 SCM415 be substituted with IS 1570 (Part 7) 10Mo6H?
KS D3867 SCM415 and IS 1570 (Part 7) 10Mo6H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.