NF A35-551 XC10 vs AS/NZS 3679.1 300

Related Material — 57.5% match based on chemical composition and mechanical property overlap.

NF A35-551 XC10 (NF A35-551:1986) and AS/NZS 3679.1 300 (AS/NZS 3679.1:2016) are both steel grades. Both fall under the Structural Steel category. NF A35-551 XC10 is typically used for fabricated parts, cold formed components, tubes, structural parts, bolts, nuts, welded assemblies, while AS/NZS 3679.1 300 is commonly used for hot-rolled structural bars and sections for general structural framing. NF A35-551 XC10 is defined under Association Francaise de Normalisation (NF), originating from France, while AS/NZS 3679.1 300 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, NF A35-551 XC10 vs AS/NZS 3679.1 300 is a 86.2% match. As per mechanical properties, the match is 0%. Combined, this makes them a related material overall at 57.5%.

Frequently Compared With NF A35-551 XC10:
CSA G40.21 400W CSA G40.21 350W CSA G40.21 260W GOST 19281 09G2S AS/NZS 3679.1 350 CSA G40.21 480W ASTM A1008 SS Grade 80 CSA G40.21 300W CSA G40.21 400A ASTM A1008 SS Grade 50 ASTM A283C ASTM A572 Gr.65
Match Breakdown
CHEMISTRY MATCH
86.2%
MECHANICAL MATCH
0%
OVERALL
57.5%
Specifications
Property NF A35-551 XC10 AS/NZS 3679.1 300
Standard NF A35-551:1986 AS/NZS 3679.1:2016
Category Structural Steel Structural Steel
C (%) 0.08-0.13 <=0.22
Si (%) <=0.35 <=0.50
Mn (%) 0.30-0.60 <=1.70
S (%) <=0.035 <=0.040
P (%) <=0.035 <=0.040
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property NF A35-551 XC10 AS/NZS 3679.1 300
Tensile Strength 320-420 MPa 440-600 MPa
Yield Strength >=210 MPa 300 MPa min
Elongation >=28% 22% min
Hardness 110-140 HB Not specified
Typical Applications
NF A35-551 XC10
fabricated parts, cold formed components, tubes, structural parts, bolts, nuts, welded assemblies
AS/NZS 3679.1 300
Hot-rolled structural bars and sections for general structural framing
Can NF A35-551 XC10 Be Substituted With AS/NZS 3679.1 300?
NF A35-551 XC10 and AS/NZS 3679.1 300 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
NF A35-551 XC10
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2500–2900 mm (98.43–114.17 in)
AS/NZS 3679.1 300
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2700–2700 mm (106.3–106.3 in)
On M-EX Right Now
NF A35-551 XC10
2 active listings and RFQs →
AS/NZS 3679.1 300
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between NF A35-551 XC10 and AS/NZS 3679.1 300?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can NF A35-551 XC10 be substituted with AS/NZS 3679.1 300?
NF A35-551 XC10 and AS/NZS 3679.1 300 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.