NF A35-552 40NCD3 vs IS 11169 (Part 1) 40Cr4Mo2

Close Alternative — 72.5% match based on chemical composition and mechanical property overlap.

NF A35-552 40NCD3 (NF A35-552:1986) and IS 11169 (Part 1) 40Cr4Mo2 (IS 11169 (Part 1):2022) are both steel grades. Both fall under the Alloy Steel category. NF A35-552 40NCD3 is typically used for used for gears, aircraft fittings, transmission shafts, crankshafts, heavy-duty bolts, and connecting rods., while IS 11169 (Part 1) 40Cr4Mo2 is commonly used for cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex c). NF A35-552 40NCD3 is defined under Association Francaise de Normalisation (NF), originating from France, while IS 11169 (Part 1) 40Cr4Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, NF A35-552 40NCD3 vs IS 11169 (Part 1) 40Cr4Mo2 is a 72.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 72.5%.

Frequently Compared With NF A35-552 40NCD3:
GOST 4543 12HN3A NF A35-565 100C6 UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10
Match Breakdown
CHEMISTRY MATCH
72.5%
MECHANICAL MATCH
No shared data
OVERALL
72.5%
Specifications
Property NF A35-552 40NCD3 IS 11169 (Part 1) 40Cr4Mo2
Standard NF A35-552:1986 IS 11169 (Part 1):2022
Category Alloy Steel Alloy Steel
C (%) 0.37-0.43 0.38-0.43
Si (%) 0.15-0.40 0.15-0.35
Mn (%) 0.50-0.80 0.75-1.00
Ni (%) 1.00-1.40 <=0.25
Cr (%) 0.60-1.00 0.80-1.10
Mo (%) 0.15-0.30 0.15-0.25
P (%) 0.035 max <=0.030
S (%) 0.035 max <=0.040
Cu (%) Not specified <=0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property NF A35-552 40NCD3 IS 11169 (Part 1) 40Cr4Mo2
Tensile Strength 850-1050 MPa Not specified
Yield Strength 650-850 MPa Not specified
Elongation 10-15% Not specified
Hardness 250-320 HB Not specified
Typical Applications
NF A35-552 40NCD3
Used for gears, aircraft fittings, transmission shafts, crankshafts, heavy-duty bolts, and connecting rods.
IS 11169 (Part 1) 40Cr4Mo2
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
Key Differences
Can NF A35-552 40NCD3 Be Substituted With IS 11169 (Part 1) 40Cr4Mo2?
NF A35-552 40NCD3 and IS 11169 (Part 1) 40Cr4Mo2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
NF A35-552 40NCD3
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6500–6600 mm (255.91–259.84 in)
IS 11169 (Part 1) 40Cr4Mo2
No active listings currently.
On M-EX Right Now
NF A35-552 40NCD3
2 active listings and RFQs →
IS 11169 (Part 1) 40Cr4Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between NF A35-552 40NCD3 and IS 11169 (Part 1) 40Cr4Mo2?
IS 11169 (Part 1) 40Cr4Mo2 specifies Cu which is not specified for NF A35-552 40NCD3.
Can NF A35-552 40NCD3 be substituted with IS 11169 (Part 1) 40Cr4Mo2?
NF A35-552 40NCD3 and IS 11169 (Part 1) 40Cr4Mo2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.