SAE J404 E52100 vs GOST 801 ShKh15

Strong Match — 87.2% match based on chemical composition and mechanical property overlap.

SAE J404 E52100 (SAE J404:2009) and GOST 801 ShKh15 (GOST 801-1978) are both steel grades. Both fall under the Alloy Steel category. SAE J404 E52100 is typically used for chemistry-only alloy steel grade; see the composition notes for product scope, while GOST 801 ShKh15 is commonly used for used for ball bearings, roller bearings, races, bearing rings, and precision rollers.. SAE J404 E52100 is defined under SAE International (United States).

As per chemical composition, SAE J404 E52100 vs GOST 801 ShKh15 is a 87.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 87.2%.

Frequently Compared With SAE J404 E52100:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 11169 (Part 1) 10Ni5Cr4 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Mo6H
Match Breakdown
CHEMISTRY MATCH
87.2%
MECHANICAL MATCH
No shared data
OVERALL
87.2%
Specifications
Property SAE J404 E52100 GOST 801 ShKh15
Standard SAE J404:2009 GOST 801-1978
Category Alloy Steel Alloy Steel
C (%) 0.98-1.10 0.95-1.05
Cr (%) 1.30-1.60 1.35-1.65
Mn (%) 0.25-0.45 0.2-0.5
P (%) <=0.025 Not specified
S (%) <=0.025 Not specified
Si (%) 0.15-0.35 0.17-0.37
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property SAE J404 E52100 GOST 801 ShKh15
Tensile Strength Not specified 750-950 MPa
Yield Strength Not specified 450 MPa min
Elongation Not specified 8% min
Hardness Not specified 60-66 HRC
Typical Applications
SAE J404 E52100
Chemistry-only alloy steel grade; see the composition notes for product scope
GOST 801 ShKh15
Used for ball bearings, roller bearings, races, bearing rings, and precision rollers.
Key Differences
Can SAE J404 E52100 Be Substituted With GOST 801 ShKh15?
SAE J404 E52100 and GOST 801 ShKh15 overlap closely enough on chemistry and mechanical properties that GOST 801 ShKh15 is often considered as a substitute for SAE J404 E52100 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
SAE J404 E52100
No active listings currently.
GOST 801 ShKh15
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6600–7000 mm (259.84–275.59 in)
On M-EX Right Now
SAE J404 E52100
0 active listings and RFQs →
GOST 801 ShKh15
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between SAE J404 E52100 and GOST 801 ShKh15?
SAE J404 E52100 specifies P, S which are not specified for GOST 801 ShKh15.
Can SAE J404 E52100 be substituted with GOST 801 ShKh15?
SAE J404 E52100 and GOST 801 ShKh15 overlap closely enough on chemistry and mechanical properties that GOST 801 ShKh15 is often considered as a substitute for SAE J404 E52100 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.