UNI 6900 X5CrNi1810 vs ASTM A959 .-

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

UNI 6900 X5CrNi1810 (UNI 6900:1971) and ASTM A959 .- (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. UNI 6900 X5CrNi1810 is typically used for used in kitchen equipment, chemical tanks, piping, architectural panels, food processing equipment, and fasteners., while ASTM A959 .- is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). UNI 6900 X5CrNi1810 is defined under Ente Nazionale Italiano di Unificazione (UNI), originating from Italy, while ASTM A959 .- is defined under ASTM International, originating from United States.

As per chemical composition, UNI 6900 X5CrNi1810 vs ASTM A959 .- is a 71.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With UNI 6900 X5CrNi1810:
GOST 5632 06Kh23N28 GB/T 3280 06Cr19Ni10 GOST 5632 12Kh13 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 EN 10088-1 1.4401 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
71.3%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property UNI 6900 X5CrNi1810 ASTM A959 .-
Standard UNI 6900:1971 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) 0.07 max <=0.030
Si (%) 1.00 max <=1.00
Mn (%) 2.00 max <=1.00
P (%) 0.045 max <=0.040
S (%) 0.015 max <=0.030
Cr (%) 17.50-19.50 18.0-20.0
Ni (%) 8.00-10.50 <=0.50
Cb (%) Not specified 0.10-0.60
N (%) Not specified <=0.030
Ti (%) Not specified 0.07-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property UNI 6900 X5CrNi1810 ASTM A959 .-
Tensile Strength 520-720 MPa Not specified
Yield Strength 210 MPa min Not specified
Elongation 45% min Not specified
Hardness 187 HB max Not specified
Typical Applications
UNI 6900 X5CrNi1810
Used in kitchen equipment, chemical tanks, piping, architectural panels, food processing equipment, and fasteners.
ASTM A959 .-
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can UNI 6900 X5CrNi1810 Be Substituted With ASTM A959 .-?
UNI 6900 X5CrNi1810 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
UNI 6900 X5CrNi1810
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2600–3700 mm (102.36–145.67 in)
ASTM A959 .-
No active listings currently.
On M-EX Right Now
UNI 6900 X5CrNi1810
2 active listings and RFQs →
ASTM A959 .-
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between UNI 6900 X5CrNi1810 and ASTM A959 .-?
ASTM A959 .- specifies Cb, N, Ti which are not specified for UNI 6900 X5CrNi1810.
Can UNI 6900 X5CrNi1810 be substituted with ASTM A959 .-?
UNI 6900 X5CrNi1810 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.