Minimal Match — 21.8% match
based on chemical composition and mechanical property overlap.
UNS C10100 and UNS C19400 are both copper grades.
Both fall under the Copper Alloys category.
UNS C10100 is defined under Unified Numbering System (UNS), originating from United States, while UNS C19400 is defined under Unified Numbering System (UNS), originating from United States.
As per chemical composition, UNS C10100 vs UNS C19400 is a 32.7% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 21.8%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
UNS C10100
UNS C19400
Yield Strength
~69 MPa (annealed O60)
~365 MPa min (H04)
Tensile Strength
~220 MPa (annealed O60)
~415-485 MPa (H04)
Elongation
~45% (annealed O60)
~3% min (H04)
Note
Oxygen-free electronic copper, values for soft annealed condition
Iron-phosphorus copper (CuFe2P), values for H04 temper per mill datasheet
Key Differences
UNS C10100 specifies Ag, As, O, Sb which are not specified for UNS C19400.
Can UNS C10100 Be Substituted With UNS C19400?
UNS C10100 and UNS C19400 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between UNS C10100 and UNS C19400?
UNS C10100 specifies Ag, As, O, Sb which are not specified for UNS C19400.
Can UNS C10100 be substituted with UNS C19400?
UNS C10100 and UNS C19400 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.