Related Material — 55.9% match
based on chemical composition and mechanical property overlap.
UNS C10100 and UNS C12000 are both copper grades.
Both fall under the Copper Alloys category.
UNS C10100 is defined under Unified Numbering System (UNS), originating from United States, while UNS C12000 is defined under Unified Numbering System (UNS), originating from United States.
As per chemical composition, UNS C10100 vs UNS C12000 is a 33.9% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a related material overall at 55.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
UNS C10100
UNS C12000
Yield Strength
~69 MPa (annealed O60)
~69 MPa (annealed O60)
Tensile Strength
~220 MPa (annealed O60)
~220 MPa (annealed O60)
Elongation
~45% (annealed O60)
~45% (annealed O60)
Note
Oxygen-free electronic copper, values for soft annealed condition
Phosphorized copper (low P), values for soft annealed condition
Key Differences
UNS C10100 specifies Pb, Zn, Fe, Ag which are not specified for UNS C12000.
Can UNS C10100 Be Substituted With UNS C12000?
UNS C10100 and UNS C12000 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between UNS C10100 and UNS C12000?
UNS C10100 specifies Pb, Zn, Fe, Ag which are not specified for UNS C12000.
Can UNS C10100 be substituted with UNS C12000?
UNS C10100 and UNS C12000 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.