Minimal Match — 50.2% match
based on chemical composition and mechanical property overlap.
UNS C14500 and UNS C10200 are both copper grades.
Both fall under the Copper Alloys category.
UNS C14500 is defined under Unified Numbering System (UNS), originating from United States, while UNS C10200 is defined under Unified Numbering System (UNS), originating from United States.
As per chemical composition, UNS C14500 vs UNS C10200 is a 75.4% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 50.2%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
UNS C14500
UNS C10200
Yield Strength
~205 MPa min (H02 half-hard)
~69 MPa (annealed O60)
Tensile Strength
~260 MPa min (H02 half-hard)
~220 MPa (annealed O60)
Elongation
~8% min (H02 half-hard)
~45% (annealed O60)
Note
Tellurium copper, values for H02 half-hard temper per mill datasheet
Oxygen-free copper, values for soft annealed condition
Key Differences
UNS C14500 specifies P, Te which are not specified for UNS C10200.
UNS C10200 specifies O which is not specified for UNS C14500.
Can UNS C14500 Be Substituted With UNS C10200?
UNS C14500 and UNS C10200 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between UNS C14500 and UNS C10200?
UNS C14500 specifies P, Te which are not specified for UNS C10200. UNS C10200 specifies O which is not specified for UNS C14500.
Can UNS C14500 be substituted with UNS C10200?
UNS C14500 and UNS C10200 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.