UNS C14500 vs UNS C12200

Related Material — 56% match based on chemical composition and mechanical property overlap.

UNS C14500 and UNS C12200 are both copper grades. Both fall under the Copper Alloys category. UNS C14500 is defined under Unified Numbering System (UNS), originating from United States, while UNS C12200 is defined under Unified Numbering System (UNS), originating from United States.

As per chemical composition, UNS C14500 vs UNS C12200 is a 84% match. As per mechanical properties, the match is 0%. Combined, this makes them a related material overall at 56%.

Frequently Compared With UNS C14500:
UNS C11000 UNS C12000 UNS C10200 UNS C10100 UNS C19400 UNS C17200
Match Breakdown
CHEMISTRY MATCH
84%
MECHANICAL MATCH
0%
OVERALL
56%
Specifications
Property UNS C14500 UNS C12200
Standard UNS UNS
Category Copper Alloys Copper Alloys
Cu (%) 99.90 min 99.90 min
P (%) 0.004-0.012 0.015-0.040
Te (%) 0.40-0.70 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property UNS C14500 UNS C12200
Yield Strength ~205 MPa min (H02 half-hard) ~69 MPa (annealed O60)
Tensile Strength ~260 MPa min (H02 half-hard) ~220 MPa (annealed O60)
Elongation ~8% min (H02 half-hard) ~45% (annealed O60)
Note Tellurium copper, values for H02 half-hard temper per mill datasheet Phosphorized copper (high P), values for soft annealed condition
Key Differences
Can UNS C14500 Be Substituted With UNS C12200?
UNS C14500 and UNS C12200 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
UNS C14500
No active listings currently.
UNS C12200
Sheet → (6 listings)
Thickness: 0.8–1.5 mm (0.03–0.06 in)
Width: 1000–1000 mm (39.37–39.37 in)
Length: 2000–2000 mm (78.74–78.74 in)
On M-EX Right Now
UNS C14500
0 active listings and RFQs →
UNS C12200
6 active listings and RFQs →
Frequently Asked Questions
What is the difference between UNS C14500 and UNS C12200?
UNS C14500 specifies Te which is not specified for UNS C12200.
Can UNS C14500 be substituted with UNS C12200?
UNS C14500 and UNS C12200 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.