AISI 1060 vs SAE J403 1065

Strong Match — 94.3% match based on chemical composition and mechanical property overlap.

AISI 1060 and SAE J403 1065 (SAE J403:2014) are both steel grades. Both fall under the Carbon Steel category. AISI 1060 is typically used for used for springs, blades, hand tools, wear parts, shafts, and cutting tools., while SAE J403 1065 is commonly used for chemistry-only grade; product scope as listed in the composition notes. AISI 1060 is defined under AISI, originating from United States, while SAE J403 1065 is defined under SAE International, originating from United States.

As per chemical composition, AISI 1060 vs SAE J403 1065 is a 94.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 94.3%.

Frequently Compared With AISI 1060:
BS 970 (Part 3) 070M55 BS 970 (Part 1) 040A10 BS 970 (Part 1) 060A62 BS 970 (Part 1) 060A57 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10
Match Breakdown
CHEMISTRY MATCH
94.3%
MECHANICAL MATCH
No shared data
OVERALL
94.3%
Specifications
Property AISI 1060 SAE J403 1065
Standard AISI SAE J403:2014
Category Carbon Steel Carbon Steel
C (%) 0.55-0.65 0.60-0.70
Mn (%) 0.60-0.90 0.60-0.90
P (%) ≤0.030 <=0.030 (flat rolled), <=0.040 (long products)
S (%) 0.050 max <=0.035 (flat rolled), <=0.050 (long products)
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property AISI 1060 SAE J403 1065
Condition Hot Rolled Not specified
Tensile Strength 700-750 MPa Not specified
Yield Strength 380-420 MPa Not specified
Elongation 11-16% Not specified
Hardness 197-220 HB Not specified
Typical Applications
AISI 1060
Used for springs, blades, hand tools, wear parts, shafts, and cutting tools.
SAE J403 1065
Chemistry-only grade; product scope as listed in the composition notes
Can AISI 1060 Be Substituted With SAE J403 1065?
AISI 1060 and SAE J403 1065 overlap closely enough on chemistry and mechanical properties that SAE J403 1065 is often considered as a substitute for AISI 1060 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
AISI 1060
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5300–6500 mm (208.66–255.91 in)
SAE J403 1065
No active listings currently.
On M-EX Right Now
AISI 1060
2 active listings and RFQs →
SAE J403 1065
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between AISI 1060 and SAE J403 1065?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can AISI 1060 be substituted with SAE J403 1065?
AISI 1060 and SAE J403 1065 overlap closely enough on chemistry and mechanical properties that SAE J403 1065 is often considered as a substitute for AISI 1060 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.