Post Stock Login Register

AISI 8615 vs GOST 4543 12HN3A

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

AISI 8615 and GOST 4543 12HN3A (GOST 4543-2016) are both steel grades. Both fall under the Alloy Steel category. AISI 8615 is typically used for used for gears, shafts, pinions, bushings, transmission parts, and carburized machinery components., while GOST 4543 12HN3A is commonly used for used for gears, pinions, crankshafts, aircraft parts, and transmission components.. AISI 8615 is defined under AISI (United States).

As per chemical composition, AISI 8615 vs GOST 4543 12HN3A is a 60.4% match. As per mechanical properties, the match is 3.6%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With AISI 8615:
NF A35-565 100C6 UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 103Cr6 IS 4367 10Cr9Mo10 IS 4367 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5
Other Alloy Steel Grades to Compare With AISI 8615:
EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
60.4%
MECHANICAL MATCH
3.6%
OVERALL
35%
Specifications
Property AISI 8615 GOST 4543 12HN3A
Standard AISI GOST 4543-2016
Category Alloy Steel Alloy Steel
C (%) 0.13-0.18 0.09-0.16
Mn (%) 0.70-0.90 0.3-0.6
Si (%) 0.15-0.35 0.17-0.37
Ni (%) 0.40-0.70 2.75-3.15
Cr (%) 0.40-0.60 0.6-0.9
Mo (%) 0.15-0.25 Not specified
P (%) 0.035 max Not specified
S (%) 0.040 max Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property AISI 8615 GOST 4543 12HN3A
Tensile Strength 700-900 MPa 850-1050 MPa
Yield Strength 500-700 MPa 685 MPa min
Elongation 14-20% 11% min
Hardness 180-240 HB 58-62 HRC (case)
Typical Applications
AISI 8615
Used for gears, shafts, pinions, bushings, transmission parts, and carburized machinery components.
GOST 4543 12HN3A
Used for gears, pinions, crankshafts, aircraft parts, and transmission components.
Key Differences
Can AISI 8615 Be Substituted With GOST 4543 12HN3A?
AISI 8615 and GOST 4543 12HN3A share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
AISI 8615
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 4900–6300 mm (192.91–248.03 in)
GOST 4543 12HN3A
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5600–6600 mm (220.47–259.84 in)
On M-EX Right Now
AISI 8615
2 active listings and RFQs →
GOST 4543 12HN3A
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between AISI 8615 and GOST 4543 12HN3A?
AISI 8615 specifies Mo, P, S which are not specified for GOST 4543 12HN3A.
Can AISI 8615 be substituted with GOST 4543 12HN3A?
AISI 8615 and GOST 4543 12HN3A share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.