ASTM A959 SS316 vs IS 1570 (Part 5) X04Cr17Ni12Mo2

Strong Match — 100% match based on chemical composition and mechanical property overlap.

ASTM A959 SS316 (ASTM A959:2011) and IS 1570 (Part 5) X04Cr17Ni12Mo2 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 SS316 is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X04Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 SS316 vs IS 1570 (Part 5) X04Cr17Ni12Mo2 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With ASTM A959 SS316:
EN 10088-1 1.4401 EN 10088-1 1.4006 EN 10088-1 1.4845 EN 10088-1 1.4301 ASTM A959 .- ASTM A959 16-8-2H GOST 5632 06Kh23N28 GOST 5632 08X18H10 GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property ASTM A959 SS316 IS 1570 (Part 5) X04Cr17Ni12Mo2
Standard ASTM A959:2011 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Cr (%) 16.0-18.0 16.0-18.0
Mn (%) <=2.00 <=2.0
Mo (%) 2.00-3.00 2.0-3.0
Ni (%) 10.0-14.0 10.0-14.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 SS316 IS 1570 (Part 5) X04Cr17Ni12Mo2
Tensile Strength Not specified >=515 MPa
Yield Strength Not specified >=205 MPa (0.2 % proof stress)
Elongation Not specified >=40% (50 mm)
Hardness Not specified <=217 HB; <=95 HRB
Condition Not specified Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Typical Applications
ASTM A959 SS316
Marine, chemical, pharmaceutical, food processing equipment
IS 1570 (Part 5) X04Cr17Ni12Mo2
Not documented
Can ASTM A959 SS316 Be Substituted With IS 1570 (Part 5) X04Cr17Ni12Mo2?
ASTM A959 SS316 and IS 1570 (Part 5) X04Cr17Ni12Mo2 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X04Cr17Ni12Mo2 is often considered as a substitute for ASTM A959 SS316 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
ASTM A959 SS316
Sheet → (24 listings)
Thickness: 2–6 mm (0.08–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–4000 mm (98.43–157.48 in)
Plate → (6 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2600–4200 mm (102.36–165.35 in)
Round Bar → (3 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 2500–4200 mm (98.43–165.35 in)
IS 1570 (Part 5) X04Cr17Ni12Mo2
No active listings currently.
On M-EX Right Now
ASTM A959 SS316
33 active listings and RFQs →
IS 1570 (Part 5) X04Cr17Ni12Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 SS316 and IS 1570 (Part 5) X04Cr17Ni12Mo2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 SS316 be substituted with IS 1570 (Part 5) X04Cr17Ni12Mo2?
ASTM A959 SS316 and IS 1570 (Part 5) X04Cr17Ni12Mo2 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X04Cr17Ni12Mo2 is often considered as a substitute for ASTM A959 SS316 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.