AS/NZS 1595 C350 vs AS/NZS 3678 Grade 350L0

Strong Match — 98.5% match based on chemical composition and mechanical property overlap.

AS/NZS 1595 C350 (AS/NZS 1595:1998) and AS/NZS 3678 Grade 350L0 (AS/NZS 3678:2016) are both steel grades. Both fall under the Structural Steel category. AS/NZS 1595 C350 is typically used for cold-rolled structural steel sheet; roll-forming, cold-formed structural sections, purlins, while AS/NZS 3678 Grade 350L0 is commonly used for refrigerated storage structures, cold climate construction, lng facility structural steel, antarctic research stations.. AS/NZS 1595 C350 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand, while AS/NZS 3678 Grade 350L0 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, AS/NZS 1595 C350 vs AS/NZS 3678 Grade 350L0 is a 97.7% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 98.5%.

Frequently Compared With AS/NZS 1595 C350:
CSA G40.21 480W CSA G40.21 300W CSA G40.21 350W ASTM A1008 SS Grade 50 CSA G40.21 400A AS/NZS 3679.1 300 CSA G40.21 400W GOST 19281 09G2S CSA G40.21 260W AS/NZS 3679.1 350 ASTM A1008 SS Grade 80 ASTM A283C
Match Breakdown
CHEMISTRY MATCH
97.7%
MECHANICAL MATCH
100%
OVERALL
98.5%
Specifications
Property AS/NZS 1595 C350 AS/NZS 3678 Grade 350L0
Standard AS/NZS 1595:1998 AS/NZS 3678:2016
Category Structural Steel Structural Steel
C (%) <=0.20 max 0.2
Mn (%) <=1.50 max 1.6
Si (%) <=0.50 max 0.55
P (%) <=0.040 max 0.03
S (%) <=0.040 max 0.03
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property AS/NZS 1595 C350 AS/NZS 3678 Grade 350L0
Tensile Strength 430 MPa min Not specified
Yield Strength 350 MPa min 350 MPa min
Elongation 14% min Not specified
Note Not specified L0 designation: low-temperature Charpy impact tested
Typical Applications
AS/NZS 1595 C350
Cold-rolled structural steel sheet; roll-forming, cold-formed structural sections, purlins
AS/NZS 3678 Grade 350L0
Refrigerated storage structures, cold climate construction, LNG facility structural steel, Antarctic research stations.
Can AS/NZS 1595 C350 Be Substituted With AS/NZS 3678 Grade 350L0?
AS/NZS 1595 C350 and AS/NZS 3678 Grade 350L0 overlap closely enough on chemistry and mechanical properties that AS/NZS 3678 Grade 350L0 is often considered as a substitute for AS/NZS 1595 C350 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
AS/NZS 1595 C350
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2500–4600 mm (98.43–181.1 in)
AS/NZS 3678 Grade 350L0
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2500–3000 mm (98.43–118.11 in)
On M-EX Right Now
AS/NZS 1595 C350
2 active listings and RFQs →
AS/NZS 3678 Grade 350L0
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between AS/NZS 1595 C350 and AS/NZS 3678 Grade 350L0?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can AS/NZS 1595 C350 be substituted with AS/NZS 3678 Grade 350L0?
AS/NZS 1595 C350 and AS/NZS 3678 Grade 350L0 overlap closely enough on chemistry and mechanical properties that AS/NZS 3678 Grade 350L0 is often considered as a substitute for AS/NZS 1595 C350 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.