ASTM A240/A240M S20432 vs ASTM A276/A276M S20100

Close Alternative — 73.8% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S20432 (ASTM A240/A240M:2025) and ASTM A276/A276M S20100 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S20432 is typically used for pressure vessels and general applications (plate, sheet and strip), while ASTM A276/A276M S20100 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished). ASTM A240/A240M S20432 is defined under ASTM International, originating from United States, while ASTM A276/A276M S20100 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A240/A240M S20432 vs ASTM A276/A276M S20100 is a 77.4% match. As per mechanical properties, the match is 66.7%. Combined, this makes them a close alternative overall at 73.8%.

Frequently Compared With ASTM A240/A240M S20432:
EN 10088-1 1.4006 EN 10088-1 1.4401 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4301 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
77.4%
MECHANICAL MATCH
66.7%
OVERALL
73.8%
Specifications
Property ASTM A240/A240M S20432 ASTM A276/A276M S20100
Standard ASTM A240/A240M:2025 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.15
Mn (%) 3.00-5.00 5.5-7.5
P (%) <=0.045 <=0.060
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 17.0-18.0 16.0-18.0
Ni (%) 4.0-6.0 3.5-5.5
N (%) 0.05-0.20 <=0.25
Cu (%) 2.00-3.00 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S20432 ASTM A276/A276M S20100
Tensile Strength >=515 MPa >=515 MPa
Yield Strength >=205 MPa >=275 MPa
Elongation >=40% >=40%
Hardness <=201 HB Not specified
Condition Plate, sheet and strip; yield by 0.2 percent offset Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Typical Applications
ASTM A240/A240M S20432
Pressure vessels and general applications (plate, sheet and strip)
ASTM A276/A276M S20100
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
Can ASTM A240/A240M S20432 Be Substituted With ASTM A276/A276M S20100?
ASTM A240/A240M S20432 and ASTM A276/A276M S20100 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A240/A240M S20432
0 active listings and RFQs →
ASTM A276/A276M S20100
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S20432 and ASTM A276/A276M S20100?
ASTM A240/A240M S20432 specifies Cu which is not specified for ASTM A276/A276M S20100.
Can ASTM A240/A240M S20432 be substituted with ASTM A276/A276M S20100?
ASTM A240/A240M S20432 and ASTM A276/A276M S20100 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.