ASTM A240/A240M:2025 S40930 Steel: Specifications & Listings

ASTM A240/A240M:2025 S40930: S40930: ferritic or martensitic (chromium) stainless steel plate, sheet and strip (UNS number, no type name printed). Specified in ASTM A240/A240M:2025. Combined limit (percent): Ti + Nb at most 0.75.

Category: Stainless Steel
Grade Details
GradeASTM A240/A240M:2025 S40930
Standard ASTM A240/A240M:2025
ApplicationsPressure vessels and general applications (plate, sheet and strip)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ASTM A959 S40910 ASTM A959:2011 USA No activity yet
ASTM A959 S40920 ASTM A959:2011 USA No activity yet
ASTM A959 S40930 ASTM A959:2011 USA No activity yet
ASTM A959 S40945 ASTM A959:2011 USA No activity yet
ASTM A959 S40976 ASTM A959:2011 USA No activity yet
ASTM A959 S41045 ASTM A959:2011 USA No activity yet
ASTM A959 S40975 ASTM A959:2011 USA No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A240/A240M S40920 ASTM A240/A240M:2025 Strong Match
ASTM A959 S40910 ASTM A959:2011 Strong Match
ASTM A959 S40920 ASTM A959:2011 Strong Match
ASTM A959 S40930 ASTM A959:2011 Strong Match
ASTM A240/A240M S40910 ASTM A240/A240M:2025 Strong Match
ASTM A959 S40945 ASTM A959:2011 Strong Match
ASTM A959 S40976 ASTM A959:2011 Strong Match
ASTM A959 S40975 ASTM A959:2011 Strong Match
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Mn P S Si Cr Ni N Ti
<=0.030 <=1.00 <=0.040 <=0.020 <=1.00 10.5-11.7 <=0.50 <=0.030 >=0.05
Mechanical Properties
Tensile Strength >=380 MPa
Yield Strength >=170 MPa
Elongation >=20%
Hardness <=179 HB
Condition Plate, sheet and strip; yield by 0.2 percent offset

More data from ASTM A240/A240M:2025

From the standard
Mechanical properties 1 condition(s)
Product or thicknessTensile strength, min (MPa)Yield strength, min (MPa)Elongation in 50 mm, min (%)
All38017020
Minimum values; yield strength by the 0.2 percent offset method.
Source: ASTM A240/A240M:2025, Table 2
Hardness 1 condition(s)
Product or thicknessBrinell HBW, maxRockwell, max
All17988 HRBW
Maximum values; either Brinell or Rockwell scale may be used.
Source: ASTM A240/A240M:2025, Table 2
Cold bend 1 value
Cold bend angle
180 deg
Bend tests are not required for chromium steels thicker than 1 in. [25 mm] or for any austenitic or duplex steel regardless of thickness.
Source: ASTM A240/A240M:2025, Table 2

Active ASTM A240/A240M:2025 S40930 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active ASTM A240/A240M:2025 S40930 listings at this time.

Register for Alerts

Buyer RFQs for ASTM A240/A240M:2025 S40930

+ Post an RFQ for this grade

No open buyer requirements for ASTM A240/A240M:2025 S40930 at this time.

Register for Alerts