ASTM A240/A240M S46800 vs ASTM A959 S44500

Close Alternative — 74.7% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S46800 (ASTM A240/A240M:2025) and ASTM A959 S44500 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S46800 is typically used for pressure vessels and general applications (plate, sheet and strip), while ASTM A959 S44500 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A240/A240M S46800 is defined under ASTM International, originating from United States, while ASTM A959 S44500 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A240/A240M S46800 vs ASTM A959 S44500 is a 74.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 74.7%.

Frequently Compared With ASTM A240/A240M S46800:
ASTM A959 .- GOST 5632 06Kh23N28 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo EN 10088-1 1.4845
Match Breakdown
CHEMISTRY MATCH
74.7%
MECHANICAL MATCH
No shared data
OVERALL
74.7%
Specifications
Property ASTM A240/A240M S46800 ASTM A959 S44500
Standard ASTM A240/A240M:2025 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.020
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.012
Si (%) <=1.00 <=1.00
Cr (%) 18.0-20.0 19.0-21.0
Ni (%) <=0.50 <=0.60
N (%) <=0.030 <=0.03
Ti (%) 0.07-0.30 Not specified
Nb (%) 0.10-0.60 Not specified
Cu (%) Not specified 0.30-0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S46800 ASTM A959 S44500
Tensile Strength >=415 MPa Not specified
Yield Strength >=205 MPa Not specified
Elongation >=22% Not specified
Hardness <=90 HRBW Not specified
Condition Plate, sheet and strip; yield by 0.2 percent offset Not specified
Typical Applications
ASTM A240/A240M S46800
Pressure vessels and general applications (plate, sheet and strip)
ASTM A959 S44500
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A240/A240M S46800 Be Substituted With ASTM A959 S44500?
ASTM A240/A240M S46800 and ASTM A959 S44500 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A240/A240M S46800
0 active listings and RFQs →
ASTM A959 S44500
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S46800 and ASTM A959 S44500?
ASTM A240/A240M S46800 specifies Ti, Nb which are not specified for ASTM A959 S44500. ASTM A959 S44500 specifies Cu which is not specified for ASTM A240/A240M S46800.
Can ASTM A240/A240M S46800 be substituted with ASTM A959 S44500?
ASTM A240/A240M S46800 and ASTM A959 S44500 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.