ASTM A240/A240M:2025 S82011: S82011: duplex (austenitic-ferritic) stainless steel plate, sheet and strip (UNS number, no type name printed). Specified in ASTM A240/A240M:2025.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Mn
P
S
Si
Cr
Ni
Mo
N
Cu
<=0.030
2.00-3.00
<=0.040
<=0.020
<=1.00
20.5-23.5
1.0-2.0
0.10-1.00
0.15-0.27
<=0.50
Mechanical Properties
Tensile Strength
>=700 MPa
Yield Strength
>=515 MPa
Elongation
>=30%
Hardness
<=293 HB
Condition
t <= 0.187 in. [5.00 mm] (first condition printed); yield by 0.2 percent offset
More data from ASTM A240/A240M:2025
From the standard
Mechanical properties2 condition(s)
Product or thickness
Tensile strength, min (MPa)
Yield strength, min (MPa)
Elongation in 50 mm, min (%)
t <= 0.187 in. [5.00 mm]
700
515
30
t > 0.187 in. [5.00 mm]
655
450
30
Minimum values; yield strength by the 0.2 percent offset method.
Source: ASTM A240/A240M:2025, Table 2
Hardness2 condition(s)
Product or thickness
Brinell HBW, max
Rockwell, max
t <= 0.187 in. [5.00 mm]
293
31 HRC
t > 0.187 in. [5.00 mm]
293
31 HRC
Maximum values; either Brinell or Rockwell scale may be used.
Source: ASTM A240/A240M:2025, Table 2
Cold bend1 value
Cold bend angle
not required
Bend tests are not required for chromium steels thicker than 1 in. [25 mm] or for any austenitic or duplex steel regardless of thickness.
Source: ASTM A240/A240M:2025, Table 2