ASTM A276/A276M S24000 vs ASTM A959 XM-28

Close Alternative — 83.2% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S24000 (ASTM A276/A276M:2017) and ASTM A959 XM-28 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S24000 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A959 XM-28 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A276/A276M S24000 is defined under ASTM International, originating from United States, while ASTM A959 XM-28 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M S24000 vs ASTM A959 XM-28 is a 83.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 83.2%.

Frequently Compared With ASTM A276/A276M S24000:
ASTM A959 .- EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
83.2%
MECHANICAL MATCH
No shared data
OVERALL
83.2%
Specifications
Property ASTM A276/A276M S24000 ASTM A959 XM-28
Standard ASTM A276/A276M:2017 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.15
Mn (%) 11.5-14.5 11.0-14.0
P (%) <=0.060 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 17.0-19.0 16.5-19.0
Ni (%) 2.3-3.7 0.50-2.50
N (%) 0.20-0.40 0.20-0.45
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S24000 ASTM A959 XM-28
Tensile Strength >=690 MPa Not specified
Yield Strength >=380 MPa Not specified
Elongation >=30% Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S24000
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A959 XM-28
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can ASTM A276/A276M S24000 Be Substituted With ASTM A959 XM-28?
ASTM A276/A276M S24000 and ASTM A959 XM-28 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A276/A276M S24000
0 active listings and RFQs →
ASTM A959 XM-28
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S24000 and ASTM A959 XM-28?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S24000 be substituted with ASTM A959 XM-28?
ASTM A276/A276M S24000 and ASTM A959 XM-28 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.