ASTM A276/A276M S32654 vs IS 6603 X01Cr24Ni22Mo7CuN
Strong Match — 86.1% match
based on chemical composition and mechanical property overlap.
ASTM A276/A276M S32654 (ASTM A276/A276M:2017) and IS 6603 X01Cr24Ni22Mo7CuN (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A276/A276M S32654 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while IS 6603 X01Cr24Ni22Mo7CuN is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars.
ASTM A276/A276M S32654 is defined under ASTM International, originating from United States, while IS 6603 X01Cr24Ni22Mo7CuN is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, ASTM A276/A276M S32654 vs IS 6603 X01Cr24Ni22Mo7CuN is a 95.8% match.
As per mechanical properties, the match is 66.7%.
Combined, this makes them a strong match overall at 86.1%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A276/A276M S32654
IS 6603 X01Cr24Ni22Mo7CuN
Tensile Strength
>=750 MPa
750-1050 MPa
Yield Strength
>=430 MPa
>=430 MPa
Elongation
>=40%
>=40%
Hardness
<=250 HB
Not specified
Condition
Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 50 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Typical Applications
ASTM A276/A276M S32654
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 6603 X01Cr24Ni22Mo7CuN
General purposes, semi-finished products, bars, wire rods and bright bars
Can ASTM A276/A276M S32654 Be Substituted With IS 6603 X01Cr24Ni22Mo7CuN?
ASTM A276/A276M S32654 and IS 6603 X01Cr24Ni22Mo7CuN overlap closely enough on chemistry and mechanical properties that IS 6603 X01Cr24Ni22Mo7CuN is often considered as a substitute for ASTM A276/A276M S32654 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between ASTM A276/A276M S32654 and IS 6603 X01Cr24Ni22Mo7CuN?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S32654 be substituted with IS 6603 X01Cr24Ni22Mo7CuN?
ASTM A276/A276M S32654 and IS 6603 X01Cr24Ni22Mo7CuN overlap closely enough on chemistry and mechanical properties that IS 6603 X01Cr24Ni22Mo7CuN is often considered as a substitute for ASTM A276/A276M S32654 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.