ASTM A276/A276M S44004 vs GOST 5632 08X18H10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S44004 (ASTM A276/A276M:2017) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S44004 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications. ASTM A276/A276M S44004 is defined under ASTM International (United States).

As per chemical composition, ASTM A276/A276M S44004 vs GOST 5632 08X18H10 is a 57.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A276/A276M S44004:
IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
57.8%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property ASTM A276/A276M S44004 GOST 5632 08X18H10
Standard ASTM A276/A276M:2017 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) 0.95-1.20 ≤0.08
Mn (%) <=1.00 ≤2.00
P (%) <=0.040 ≤0.035
S (%) <=0.030 ≤0.020
Si (%) <=1.00 ≤0.80
Cr (%) 16.0-18.0 17.0–19.0
Mo (%) <=0.75 Not specified
Ni (%) Not specified 9.0–11.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S44004 GOST 5632 08X18H10
Hardness <=269 HB Not specified
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Not specified
Tensile Strength Not specified ≥520 MPa
Yield Strength Not specified ≥205 MPa
Elongation Not specified ≥40%
Typical Applications
ASTM A276/A276M S44004
Stainless steel bars and shapes (hot-finished or cold-finished)
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
Can ASTM A276/A276M S44004 Be Substituted With GOST 5632 08X18H10?
ASTM A276/A276M S44004 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S44004
No active listings currently.
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
ASTM A276/A276M S44004
0 active listings and RFQs →
GOST 5632 08X18H10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S44004 and GOST 5632 08X18H10?
ASTM A276/A276M S44004 specifies Mo which is not specified for GOST 5632 08X18H10. GOST 5632 08X18H10 specifies Ni which is not specified for ASTM A276/A276M S44004.
Can ASTM A276/A276M S44004 be substituted with GOST 5632 08X18H10?
ASTM A276/A276M S44004 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.