ASTM A276/A276M S44004 vs IS 1570 (Part 7) 12Cr13H

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S44004 (ASTM A276/A276M:2017) and IS 1570 (Part 7) 12Cr13H (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S44004 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while IS 1570 (Part 7) 12Cr13H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. ASTM A276/A276M S44004 is defined under ASTM International, originating from United States, while IS 1570 (Part 7) 12Cr13H is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A276/A276M S44004 vs IS 1570 (Part 7) 12Cr13H is a 67.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A276/A276M S44004:
IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
67.6%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property ASTM A276/A276M S44004 IS 1570 (Part 7) 12Cr13H
Standard ASTM A276/A276M:2017 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) 0.95-1.20 0.09-0.15
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 16.0-18.0 11.5-14.00
Mo (%) <=0.75 Not specified
Ni (%) Not specified <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S44004 IS 1570 (Part 7) 12Cr13H
Hardness <=269 HB Not specified
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Bars, forgings, plates, A, thickness up to 160 (first row of Table 3)
Tensile Strength Not specified 470-670 MPa
Yield Strength Not specified >=265 MPa (0.2 % proof stress)
Elongation Not specified >=20%
Typical Applications
ASTM A276/A276M S44004
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 1570 (Part 7) 12Cr13H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can ASTM A276/A276M S44004 Be Substituted With IS 1570 (Part 7) 12Cr13H?
ASTM A276/A276M S44004 and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S44004
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr13H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S44004 and IS 1570 (Part 7) 12Cr13H?
ASTM A276/A276M S44004 specifies Mo which is not specified for IS 1570 (Part 7) 12Cr13H. IS 1570 (Part 7) 12Cr13H specifies Ni which is not specified for ASTM A276/A276M S44004.
Can ASTM A276/A276M S44004 be substituted with IS 1570 (Part 7) 12Cr13H?
ASTM A276/A276M S44004 and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.