ASTM A276/A276M:2017 S82441 Steel: Specifications & Listings

ASTM A276/A276M:2017 S82441: S82441: austenitic-ferritic (duplex) stainless steel bars and shapes (UNS number, no type name printed). Specified in ASTM A276/A276M:2017.

Category: Stainless Steel
Grade Details
GradeASTM A276/A276M:2017 S82441
Standard ASTM A276/A276M:2017
ApplicationsStainless steel bars and shapes (hot-finished or cold-finished)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ASTM A240/A240M S82441 ASTM A240/A240M:2025 USA No activity yet
EN 10088-1 X2CrNiMnMoCuN24-4-3-2 EN 10088-1:2014 Europe (CEN) No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A240/A240M S82441 ASTM A240/A240M:2025 Strong Match
EN 10088-1 X2CrNiMnMoCuN24-4-3-2 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrNiMnMoCuN24-4-3-2 EN 10088-1:2023 Strong Match
IS 6603 X02Cr24Ni4Mn3Mo2CuN IS 6603:2024 Close Alternative
EN 10088-3 X2CrNiMnMoCuN24-4-3-2 EN 10088-3:2014 Close Alternative
ASTM A959 S32950 ASTM A959:2011 Related Material
EN 10088-1 X1CrNiMoCuN24-22-8 EN 10088-1:2014 Related Material
EN 10088-1 X1CrNiMoCuN24-22-8 EN 10088-1:2023 Related Material
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Mn P S Cr Ni Mo N Cu
<=0.030 2.5-4.0 <=0.035 <=0.005 23.0-25.0 3.0-4.5 1.00-2.00 0.20-0.30 0.10-0.80
Mechanical Properties
Tensile Strength >=740 MPa
Yield Strength >=540 MPa
Elongation >=25%
Hardness <=290 HB
Condition Condition A (Annealed), hot-finished or cold-finished, under 7/16 [11 mm] sizes (first row printed)

More data from ASTM A276/A276M:2017

From the standard
Mechanical requirements by condition and size 2 row(s)
ConditionFinishDiameter or thickness, in. [mm]Tensile strength, min (MPa)Yield strength, min (MPa)Elongation, min (%)Reduction of area, min (%)Brinell HBW, max
A (Annealed)hot-finished or cold-finishedunder 7/16 [11 mm]74054025-290
A (Annealed)hot-finished or cold-finished7/16 [11 mm] and over68048025-290
Yield by the 0.2 percent offset method. Hardness is HBW unless otherwise indicated; equivalent Rockwell is permitted.
Source: ASTM A276/A276M:2017, Table 2

Active ASTM A276/A276M:2017 S82441 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active ASTM A276/A276M:2017 S82441 listings at this time.

Register for Alerts

Buyer RFQs for ASTM A276/A276M:2017 S82441

+ Post an RFQ for this grade

No open buyer requirements for ASTM A276/A276M:2017 S82441 at this time.

Register for Alerts