ASTM A276/A276M S82441 vs IS 6603 X02Cr24Ni4Mn3Mo2CuN
Close Alternative — 79.9% match
based on chemical composition and mechanical property overlap.
ASTM A276/A276M S82441 (ASTM A276/A276M:2017) and IS 6603 X02Cr24Ni4Mn3Mo2CuN (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A276/A276M S82441 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while IS 6603 X02Cr24Ni4Mn3Mo2CuN is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars.
ASTM A276/A276M S82441 is defined under ASTM International, originating from United States, while IS 6603 X02Cr24Ni4Mn3Mo2CuN is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, ASTM A276/A276M S82441 vs IS 6603 X02Cr24Ni4Mn3Mo2CuN is a 94.8% match.
As per mechanical properties, the match is 50%.
Combined, this makes them a close alternative overall at 79.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A276/A276M S82441
IS 6603 X02Cr24Ni4Mn3Mo2CuN
Tensile Strength
>=740 MPa
>=650 MPa
Yield Strength
>=540 MPa
>=450 MPa
Elongation
>=25%
>=25%
Hardness
<=290 HB
<=290 HB
Condition
Condition A (Annealed), hot-finished or cold-finished, under 7/16 [11 mm] sizes (first row printed)
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Tensile Strength is a minimum as printed, hardness for guidance only
Typical Applications
ASTM A276/A276M S82441
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 6603 X02Cr24Ni4Mn3Mo2CuN
General purposes, semi-finished products, bars, wire rods and bright bars
Key Differences
IS 6603 X02Cr24Ni4Mn3Mo2CuN specifies Si which is not specified for ASTM A276/A276M S82441.
Can ASTM A276/A276M S82441 Be Substituted With IS 6603 X02Cr24Ni4Mn3Mo2CuN?
ASTM A276/A276M S82441 and IS 6603 X02Cr24Ni4Mn3Mo2CuN are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between ASTM A276/A276M S82441 and IS 6603 X02Cr24Ni4Mn3Mo2CuN?
IS 6603 X02Cr24Ni4Mn3Mo2CuN specifies Si which is not specified for ASTM A276/A276M S82441.
Can ASTM A276/A276M S82441 be substituted with IS 6603 X02Cr24Ni4Mn3Mo2CuN?
ASTM A276/A276M S82441 and IS 6603 X02Cr24Ni4Mn3Mo2CuN are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.