ASTM A276/A276M S82441 vs EN 10088-1 X1CrNiMoCuN24-22-8

Related Material — 66.6% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S82441 (ASTM A276/A276M:2017) and EN 10088-1 X1CrNiMoCuN24-22-8 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S82441 is defined under ASTM International, originating from United States, while EN 10088-1 X1CrNiMoCuN24-22-8 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S82441 vs EN 10088-1 X1CrNiMoCuN24-22-8 is a 66.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 66.6%.

Frequently Compared With ASTM A276/A276M S82441:
EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
66.6%
MECHANICAL MATCH
No shared data
OVERALL
66.6%
Specifications
Property ASTM A276/A276M S82441 EN 10088-1 X1CrNiMoCuN24-22-8
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.020
Mn (%) 2.5-4.0 2.00-4.0
P (%) <=0.035 <=0.030
S (%) <=0.005 <=0.005
Cr (%) 23.0-25.0 23.0-25.0
Ni (%) 3.0-4.5 21.0-23.0
Mo (%) 1.00-2.00 7.0-8.0
N (%) 0.20-0.30 0.45-0.55
Cu (%) 0.10-0.80 0.30-0.60
Si (%) Not specified <=0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S82441 EN 10088-1 X1CrNiMoCuN24-22-8
Tensile Strength >=740 MPa Not specified
Yield Strength >=540 MPa Not specified
Elongation >=25% Not specified
Hardness <=290 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, under 7/16 [11 mm] sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S82441
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 X1CrNiMoCuN24-22-8
Not documented
Key Differences
Can ASTM A276/A276M S82441 Be Substituted With EN 10088-1 X1CrNiMoCuN24-22-8?
ASTM A276/A276M S82441 and EN 10088-1 X1CrNiMoCuN24-22-8 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S82441
0 active listings and RFQs →
EN 10088-1 X1CrNiMoCuN24-22-8
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S82441 and EN 10088-1 X1CrNiMoCuN24-22-8?
EN 10088-1 X1CrNiMoCuN24-22-8 specifies Si which is not specified for ASTM A276/A276M S82441.
Can ASTM A276/A276M S82441 be substituted with EN 10088-1 X1CrNiMoCuN24-22-8?
ASTM A276/A276M S82441 and EN 10088-1 X1CrNiMoCuN24-22-8 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.