ASTM A514 vs IS 1570 (Part 7) 10Cr36Mo10H

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A514 (ASTM A514) and IS 1570 (Part 7) 10Cr36Mo10H (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Alloy Steel category. ASTM A514 is typically used for used for cranes, mining equipment, pressure vessels, bridges, heavy trucks, and structural fabrication., while IS 1570 (Part 7) 10Cr36Mo10H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. ASTM A514 is defined under ASTM International, originating from United States, while IS 1570 (Part 7) 10Cr36Mo10H is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A514 vs IS 1570 (Part 7) 10Cr36Mo10H is a 55.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A514:
GOST 4543 12HN3A NF A35-565 100C6 UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 103Cr6 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
55.8%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property ASTM A514 IS 1570 (Part 7) 10Cr36Mo10H
Standard ASTM A514 IS 1570 (Part 7):1992
Category Alloy Steel Alloy Steel
C (%) 0.12-0.21 <=0.15
Mn (%) 0.70-1.60 0.30-0.60
Si (%) 0.15-0.40 0.25-1.0
Cr (%) 0.40-1.50 8.00-10.00
Mo (%) 0.15-0.60 0.90-1.10
Ni (%) 0.40-1.00 Not specified
P (%) 0.035 max <=0.040
S (%) 0.035 max <=0.030
Al (metallic) (%) Not specified <=0.02
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A514 IS 1570 (Part 7) 10Cr36Mo10H
Tensile Strength 760-895 MPa 410-560 MPa
Yield Strength 690 MPa min >=135 MPa (0.2 % proof stress)
Elongation 16-18% >=20%
Hardness 235-293 HB Not specified
Condition Not specified Pipes, A, thickness - (first row of Table 3)
Typical Applications
ASTM A514
Used for cranes, mining equipment, pressure vessels, bridges, heavy trucks, and structural fabrication.
IS 1570 (Part 7) 10Cr36Mo10H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can ASTM A514 Be Substituted With IS 1570 (Part 7) 10Cr36Mo10H?
ASTM A514 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A514
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5800–6500 mm (228.35–255.91 in)
IS 1570 (Part 7) 10Cr36Mo10H
No active listings currently.
On M-EX Right Now
ASTM A514
2 active listings and RFQs →
IS 1570 (Part 7) 10Cr36Mo10H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A514 and IS 1570 (Part 7) 10Cr36Mo10H?
ASTM A514 specifies Ni which is not specified for IS 1570 (Part 7) 10Cr36Mo10H. IS 1570 (Part 7) 10Cr36Mo10H specifies Al (metallic) which is not specified for ASTM A514.
Can ASTM A514 be substituted with IS 1570 (Part 7) 10Cr36Mo10H?
ASTM A514 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.