ASTM A514 vs IS 4367 10Cr9Mo10

Minimal Match — 38.9% match based on chemical composition and mechanical property overlap.

ASTM A514 (ASTM A514) and IS 4367 10Cr9Mo10 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. ASTM A514 is defined under ASTM International, originating from United States, while IS 4367 10Cr9Mo10 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A514 vs IS 4367 10Cr9Mo10 is a 58.4% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 38.9%.

Frequently Compared With ASTM A514:
GOST 4543 12HN3A NF A35-565 100C6 UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 103Cr6 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
58.4%
MECHANICAL MATCH
0%
OVERALL
38.9%
Specifications
Property ASTM A514 IS 4367 10Cr9Mo10
Standard ASTM A514 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.12-0.21 <=0.15
Mn (%) 0.70-1.60 0.40-0.70
Si (%) 0.15-0.40 <=0.50
Cr (%) 0.40-1.50 2.00-2.50
Mo (%) 0.15-0.60 0.90-1.10
Ni (%) 0.40-1.00 <=0.30
P (%) 0.035 max <=0.035
S (%) 0.035 max <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A514 IS 4367 10Cr9Mo10
Tensile Strength 760-895 MPa 410-590 MPa
Yield Strength 690 MPa min 245 MPa min
Elongation 16-18% >=18%
Hardness 235-293 HB Not specified
Izod Impact Not specified 55 J min
Hardness (soft annealed) Not specified <=187 HB
Condition Not specified Normalised and tempered, ruling section up to 50 mm
Typical Applications
ASTM A514
Used for cranes, mining equipment, pressure vessels, bridges, heavy trucks, and structural fabrication.
IS 4367 10Cr9Mo10
Not documented
Can ASTM A514 Be Substituted With IS 4367 10Cr9Mo10?
ASTM A514 and IS 4367 10Cr9Mo10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A514
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5800–6500 mm (228.35–255.91 in)
IS 4367 10Cr9Mo10
No active listings currently.
On M-EX Right Now
ASTM A514
2 active listings and RFQs →
IS 4367 10Cr9Mo10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A514 and IS 4367 10Cr9Mo10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A514 be substituted with IS 4367 10Cr9Mo10?
ASTM A514 and IS 4367 10Cr9Mo10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.