ASTM A959 616 vs ASTM A959 S42225

Strong Match — 85.4% match based on chemical composition and mechanical property overlap.

ASTM A959 616 (ASTM A959:2011) and ASTM A959 S42225 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 616 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A959 S42225 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A959 616 is defined under ASTM International, originating from United States, while ASTM A959 S42225 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 616 vs ASTM A959 S42225 is a 85.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 85.4%.

Frequently Compared With ASTM A959 616:
IS 1570 (Part 7) 20Cr12MoNiVH EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 08X18H10 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
85.4%
MECHANICAL MATCH
No shared data
OVERALL
85.4%
Specifications
Property ASTM A959 616 ASTM A959 S42225
Standard ASTM A959:2011 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) 0.20-0.25 0.20-0.25
Cr (%) 11.0-12.5 11.0-12.5
Mn (%) 0.50-1.00 0.50-1.00
Mo (%) 0.90-1.25 0.90-1.25
Ni (%) 0.50-1.00 0.50-1.00
P (%) <=0.025 <=0.020
S (%) <=0.025 <=0.010
Si (%) <=0.50 0.20-0.50
V (%) 0.20-0.30 0.20-0.30
W (%) 0.90-1.25 0.90-1.25
Al (%) Not specified <=0.025
Cb (%) Not specified <=0.05
Co (%) Not specified <=0.20
Cu (%) Not specified <=0.15
Sn (%) Not specified <=0.02
Ti (%) Not specified <=0.025
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
ASTM A959 616
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A959 S42225
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A959 616 Be Substituted With ASTM A959 S42225?
ASTM A959 616 and ASTM A959 S42225 overlap closely enough on chemistry and mechanical properties that ASTM A959 S42225 is often considered as a substitute for ASTM A959 616 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 616
0 active listings and RFQs →
ASTM A959 S42225
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 616 and ASTM A959 S42225?
ASTM A959 S42225 specifies Al, Cb, Co, Cu which are not specified for ASTM A959 616.
Can ASTM A959 616 be substituted with ASTM A959 S42225?
ASTM A959 616 and ASTM A959 S42225 overlap closely enough on chemistry and mechanical properties that ASTM A959 S42225 is often considered as a substitute for ASTM A959 616 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.