ASTM A959 S32615 vs IS 11169 (Part 2) X04Cr17Ni12Mo2Ti

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A959 S32615 (ASTM A959:2011) and IS 11169 (Part 2) X04Cr17Ni12Mo2Ti (IS 11169 (Part 2):2023) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S32615 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 11169 (Part 2) X04Cr17Ni12Mo2Ti is commonly used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11). ASTM A959 S32615 is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X04Cr17Ni12Mo2Ti is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 S32615 vs IS 11169 (Part 2) X04Cr17Ni12Mo2Ti is a 71.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A959 S32615:
GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
71.2%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A959 S32615 IS 11169 (Part 2) X04Cr17Ni12Mo2Ti
Standard ASTM A959:2011 IS 11169 (Part 2):2023
Category Stainless Steel Stainless Steel
C (%) <=0.07 <=0.08
Cr (%) 16.5-19.5 16.5-18.5
Cu (%) 1.50-2.50 <=1.00
Mn (%) <=2.00 <=2.00
Mo (%) 0.30-1.50 2.00-2.50
Ni (%) 19.0-22.0 10.5-13.5
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) 4.8-6.0 <=1.00
Ti (%) Not specified 5xC-0.70
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S32615 IS 11169 (Part 2) X04Cr17Ni12Mo2Ti
Reduction of Area, solution annealed (+AT) Not specified >=65% (over 5 to 50 mm)
Tensile Strength, solution annealed (+AT) Not specified <=680 MPa (over 5 to 50 mm)
Typical Applications
ASTM A959 S32615
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
Key Differences
Can ASTM A959 S32615 Be Substituted With IS 11169 (Part 2) X04Cr17Ni12Mo2Ti?
ASTM A959 S32615 and IS 11169 (Part 2) X04Cr17Ni12Mo2Ti share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A959 S32615
0 active listings and RFQs →
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S32615 and IS 11169 (Part 2) X04Cr17Ni12Mo2Ti?
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti specifies Ti which is not specified for ASTM A959 S32615.
Can ASTM A959 S32615 be substituted with IS 11169 (Part 2) X04Cr17Ni12Mo2Ti?
ASTM A959 S32615 and IS 11169 (Part 2) X04Cr17Ni12Mo2Ti share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.