Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
ASTM A959 S38400 (ASTM A959:2011) and IS 11169 (Part 2) X02Cr19Ni10 (IS 11169 (Part 2):1989) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A959 S38400 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 11169 (Part 2) X02Cr19Ni10 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1).
ASTM A959 S38400 is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, ASTM A959 S38400 vs IS 11169 (Part 2) X02Cr19Ni10 is a 81.3% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 69.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A959 S38400
IS 11169 (Part 2) X02Cr19Ni10
Yield Strength (0.2% proof)
Not specified
>=175 MPa
Tensile Strength
Not specified
450-700 MPa
Elongation
Not specified
>=50%
Impact (U-notch 5 mm)
Not specified
>=60 J
Condition
Not specified
Quenched reference test piece (Table 6 treatment)
Typical Applications
ASTM A959 S38400
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 11169 (Part 2) X02Cr19Ni10
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
Can ASTM A959 S38400 Be Substituted With IS 11169 (Part 2) X02Cr19Ni10?
ASTM A959 S38400 and IS 11169 (Part 2) X02Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between ASTM A959 S38400 and IS 11169 (Part 2) X02Cr19Ni10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 S38400 be substituted with IS 11169 (Part 2) X02Cr19Ni10?
ASTM A959 S38400 and IS 11169 (Part 2) X02Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.