ASTM A959 S41428 vs EN 10088-1 1.4401

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A959 S41428 (ASTM A959:2011) and EN 10088-1 1.4401 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S41428 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while EN 10088-1 1.4401 is commonly used for marine, chemical processing, pharmaceutical equipment. ASTM A959 S41428 is defined under ASTM International, originating from United States, while EN 10088-1 1.4401 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A959 S41428 vs EN 10088-1 1.4401 is a 37.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A959 S41428:
IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
37.6%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property ASTM A959 S41428 EN 10088-1 1.4401
Standard ASTM A959:2011 EN 10088-1:2014
Category Stainless Steel Stainless Steel
Al (%) <=0.025 Not specified
C (%) 0.10-0.17 ≤0.07
Cr (%) 11.3-12.7 16.5–18.5
Cu (%) <=0.15 Not specified
Mn (%) 0.65-1.05 ≤2.00
Mo (%) 1.50-2.00 2.0–2.5
N (%) 0.020-0.045 Not specified
Ni (%) 2.3-3.2 10.5–13.5
P (%) <=0.020 Not specified
S (%) <=0.015 Not specified
Si (%) 0.10-0.35 ≤1.00
Sn (%) <=0.05 Not specified
Ti (%) <=0.05 Not specified
V (%) 0.25-0.40 Not specified
W (%) <=0.10 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S41428 EN 10088-1 1.4401
Tensile Strength Not specified ≥520 MPa
Yield Strength Not specified ≥210 MPa
Elongation Not specified ≥40%
Hardness Not specified ≤215 HB
Typical Applications
ASTM A959 S41428
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
EN 10088-1 1.4401
Marine, chemical processing, pharmaceutical equipment
Key Differences
Can ASTM A959 S41428 Be Substituted With EN 10088-1 1.4401?
ASTM A959 S41428 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A959 S41428
No active listings currently.
EN 10088-1 1.4401
Sheet → (4 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3400 mm (98.43–133.86 in)
On M-EX Right Now
ASTM A959 S41428
0 active listings and RFQs →
EN 10088-1 1.4401
4 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S41428 and EN 10088-1 1.4401?
ASTM A959 S41428 specifies Al, Cu, N, P which are not specified for EN 10088-1 1.4401.
Can ASTM A959 S41428 be substituted with EN 10088-1 1.4401?
ASTM A959 S41428 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.