BS 970 (Part 1) 832H13 vs BS 970 (Part 1) 832M13

Strong Match — 98.6% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 832H13 (BS 970 (Part 1):1983) and BS 970 (Part 1) 832M13 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 832H13 is typically used for case hardening steel supplied to specified hardenability limits (end quench test, table 10)., while BS 970 (Part 1) 832M13 is commonly used for case hardening steel (section four). BS 970 (Part 1) 832H13 is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 832M13 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 (Part 1) 832H13 vs BS 970 (Part 1) 832M13 is a 98.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98.6%.

Frequently Compared With BS 970 (Part 1) 832H13:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 NF A35-565 100C6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H UNI 11234 100Cr6
Match Breakdown
CHEMISTRY MATCH
98.6%
MECHANICAL MATCH
No shared data
OVERALL
98.6%
Specifications
Property BS 970 (Part 1) 832H13 BS 970 (Part 1) 832M13
Standard BS 970 (Part 1):1983 BS 970 (Part 1):1991
Category Alloy Steel Alloy Steel
C (%) 0.10-0.16 0.10-0.16
Mn (%) 0.35-0.60 0.35-0.60
Cr (%) 0.70-1.00 0.70-1.00
Mo (%) 0.10-0.25 0.10-0.25
Ni (%) 3.00-3.75 3.00-3.75
P (%) <=0.035 Not specified
S (%) <=0.040 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 832H13 BS 970 (Part 1) 832M13
Condition Not specified Case hardened, 19 mm test bar
Tensile Strength Not specified 1080 MPa min
Elongation Not specified 8 % min
Typical Applications
BS 970 (Part 1) 832H13
Case hardening steel supplied to specified hardenability limits (end quench test, Table 10).
BS 970 (Part 1) 832M13
Case hardening steel (section four)
Key Differences
Can BS 970 (Part 1) 832H13 Be Substituted With BS 970 (Part 1) 832M13?
BS 970 (Part 1) 832H13 and BS 970 (Part 1) 832M13 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 832M13 is often considered as a substitute for BS 970 (Part 1) 832H13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 832H13
0 active listings and RFQs →
BS 970 (Part 1) 832M13
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 832H13 and BS 970 (Part 1) 832M13?
BS 970 (Part 1) 832H13 specifies P, S which are not specified for BS 970 (Part 1) 832M13.
Can BS 970 (Part 1) 832H13 be substituted with BS 970 (Part 1) 832M13?
BS 970 (Part 1) 832H13 and BS 970 (Part 1) 832M13 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 832M13 is often considered as a substitute for BS 970 (Part 1) 832H13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.